The invention discloses a low smoke halogen-free flame retardant polyolefin cable material irradiated by 125 DEG radiation, belonging to the field of cable material formula. EVA60-90, HDPE40-60, 45-60, 45-60 aluminum hydroxide, magnesium hydroxide, calcium zinc composite stabilizer 5-10, strong agent 10-15, flame retardant 5-10, compatible agent 10-18, antioxidant OSP-11-1.5, crosslinking agent, lubricant 0.5-1 portions, 4-6. The present invention is a kind of environmental friendly cable material satisfying low smoke, halogen-free, non-toxic, flame retardant and high temperature resistance. At the same time, its mechanical properties, processability, flame retardance and high temperature resistance all reach a higher level.
【技术实现步骤摘要】
一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料
本专利技术属于一种电缆料配方,具体地说,尤其涉及一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料。
技术介绍
125℃辐照交联低烟无卤阻燃聚烯烃电缆料是为满足低烟、无卤无毒、阻燃、耐高温等特性而开发的一种环保型阻燃电缆材料。它是使用聚烯烃作为基材,氢氧化铝、氢氧化镁等无机阻燃材料作阻燃剂,经共混、塑化、造粒而成的可辐照交联电缆料。125℃辐照交联低烟无卤阻燃聚烯烃电缆料的开发,要解决如下几个技术关键:(1)由于不能使用含有卤素的阻燃剂,而只能使用氢氧化铝、氢氧化镁、硼酸锌等无毒的无机阻燃剂,这些阻燃剂需要添加50%~60%(重量百分比)才起到很好的阻燃作用,而无机阻燃剂的大量添加则大幅度降低材料的机械性能,所以如何保证机械性能与阻燃性能的平衡,此为最重要的技术关键。(2)在添加大量的无机阻燃剂后,材料的加工流动性很差,螺杆扭矩急剧上升,使得造粒生产非常困难,绝缘挤出也很困难,如何改善这些材料的加工性能即为第二个技术关键。(3)如果材料在燃烧时熔融滴落,更易使火灾蔓延,加剧火情,也使材料暴露出新的表面加速燃烧。为此,防滴落便成为开发这一产品的另一个技术攻关难点。(4)材料要求的耐温等级为125℃,为使材料能达到这个等级要求,就要很好地解决材料的耐热老化问题。
技术实现思路
本专利技术目的是提供一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料,以克服现有技术中的上述缺陷。本专利技术是采用以下技术方案实现的:一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料,包括以下重量比配方:EVA60-90份、HDPE40-60份、氢氧化铝45- ...
【技术保护点】
一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料,其特征在于,包括以下重量比配方:EVA60‑90份、HDPE40‑60份、氢氧化铝45‑60份、氢氧化镁45‑60份、钙锌复合稳定剂5‑10份、柔强剂10‑15份、阻燃剂5‑10份、相容剂10‑18份、抗氧剂OSP‑11‑1.5份、润滑剂0.5‑1份、交联剂4‑6份。
【技术特征摘要】
1.一种125℃辐照交联低烟无卤阻燃聚烯烃电缆料,其特征在于,包括以下重量比配方:EVA60-90份、HDPE40-60份、氢氧化铝45-60份、氢氧化镁45-60份、钙锌复合稳定剂5-10份、柔强剂10-15份、阻燃剂5-10份、相容剂10-18份、抗氧剂OSP-11-1.5份、润滑剂0.5-1份、交联剂4-6份。2.根据权利要求1所述的125℃辐照...
【专利技术属性】
技术研发人员:李春花,
申请(专利权)人:青岛祥智电子技术有限公司,
类型:发明
国别省市:山东,37