The utility model relates to a clay board, belonging to the technical field of building materials. The invention comprises the following components: weight of illite, kaolin, 10-35 0-15 pyrophyllite 5-15 parts, porcelain stone 5-30, smelting of iron ore tailings 20-50, coarse poor materials 5-30, plasticizer 0-5, 20-40 powder, clay clay powder, feldspar powder 10-20 parts 20-30 20-30, aggregate. The aggregate is broken from waste tiles, tiles, pottery bricks and their leftover materials, with a fineness of 12-60 mesh. The damage to human organic radiation, the invention of stone artificial stone; high temperature burning high strength, never fade, not affected by climate and environment; through the bold in the formulation of the aggregate, can make the clay plate surface roughness will not slip; the invention of clay plate extrusion drying fast, high pass rate, firing cycle three short, save, use of iron ore tailings, local industrial waste reuse.
【技术实现步骤摘要】
一种陶土板
本专利技术涉及一种陶土板，属于建筑材料
技术介绍
陶土，是指含有铁质而带黄褐色、灰白色、红紫色等色调，具有良好可塑性的粘土。陶土是陶器原料。矿物成分复杂，主要由高岭石、水白云母、蒙脱石、石英和长石组成。颗粒大小不一致，常含砂粒、粉砂和粘土等。具吸水性和吸附性，加水后有可塑性。颜色不纯，往往带有黄、灰等色，因而仅用于陶器制造。陶土主要用作烧制外墙、地砖、陶器具等。陶土具有以下特性：1、优异的抗冻融特性：在吸水率达到10％的情况下，瓷质砖在-15℃时冻融三次已经全部冻裂，而陶砖却可以在-45℃的环境下冻融50次不出现裂痕。2、良好的抗光污染性能：陶砖能够将90％以上的光全部折射，对保护人体视力、减少光污染有很好的作用。3、良好的吸音作用：由于陶砖通体富含大量均匀细蜜的开放性气孔，故能将声波全部或部分折射出去，取到室外降低噪音，室内消除回音的效果，是创造城市优良居住环境的绝佳材料。4、良好的透气性、透水性：陶砖透气、透水的优越性在绿色文明的今天得到充分的展示，其古朴的韵味与自然景观相融合，体现了人与自然的和谐对话。5、良好的耐风化耐腐蚀性：随着工业污染的加重，雨水中的酸性一天天在增加，很多建筑材料因为无法接受这个考验而被淘汰。纯天然的加工工序使得陶砖本身只含有少量的化学杂质，其内部结构也不易受到酸雨的影响，陶土抗碱腐蚀性的特性更的其他材料无法与之相比的。
技术实现思路
本专利技术的目的是提供一种陶土板。本专利技术的技术方案包括如下：本专利技术陶土板由以下重量份的物质组成：伊利土10-35份、高岭土0-15份、叶腊石5-15份、瓷石5-30份、冶...
【技术保护点】
一种陶土板，其特征在于，所述的陶土板由以下重量份的物质组成：伊利土10‑35份、高岭土0‑15份、叶腊石5‑15份、瓷石5‑30份、冶炼铁矿的尾渣20‑50份、粗瘠性料5‑30份、增塑剂0‑5份、陶土干粉20‑40份、瓷土干粉20‑30份、长石粉10‑20份、骨料20‑30份。
【技术特征摘要】
1.一种陶土板，其特征在于，所述的陶土板由以下重量份的物质组成：伊利土10-35份、高岭土0-15份、叶腊石5-15份、瓷石5-30份、冶炼铁矿的尾渣20-50份、粗瘠性料5-30份、增塑剂0-5份、...