The invention discloses a wollastonite fiber preparation method comprises the following steps: A, 990g, CaF210g from natural wollastonite, these raw materials by grinding into 10 mm below the particle; B, the raw material powder into the furnace, heating to 1500-1600 DEG C melting; C, melting in the exit, with silk throwing machine by centrifugation throwing wire; D, silk fibers entered the collector to get wollastonite fiber products. The wollastonite fiber preparation method by melting wollastonite and fused siliceous raw material and limestone with wollastonite blow pull long fiber asbestos use requirements, to completely replace the asbestos fiber wollastonite; tensile strength was 25 x 102MPa - 25 x 102MPa; thermal conductivity under 300 DEG C: 13 14W/m K.
【技术实现步骤摘要】
一种硅灰石纤维制备方法
本专利技术涉及一种制备硅灰石纤维的方法，尤其涉及一种能完全取代石棉的硅灰石纤维制备方法。
技术介绍
石棉纤维对人体有害，许多国家已经禁止使用，现已用天然硅灰石部分替代，但是，由于天然硅灰石的纤维短，限制了它在某些方面的应用，因而不能完全取代石棉。因此，寻找和生产对人体无害、具有较好抗拉强度和较高热导率的长纤维矿物来完全取代石棉纤维，己经迫在眉睫。
技术实现思路
本专利技术所要解决的技术问题是克服现有技术的缺陷，提供一种硅灰石纤维制备方法，该硅灰石纤维制备方法通过将熔融的硅灰石或熔融的含硅质原料与石灰石吹拉成符合石棉用途要求指标的硅灰石长纤维，达到完全取代石棉的目的；制得的硅灰石长纤维抗拉强度：25x102MPa-25x102MPa；300℃下热导率：13一14W/m·K。本专利技术解决其技术问题所采用的技术方案是：一种硅灰石纤维制备方法，包括以下步骤：a、称取天然硅灰石990g、CaF210g，将这些原料通过磨机粉碎成10毫米以下的颗粒；b、将原料粉末投入电阻炉中，加热至1500-1600℃熔融；c、在熔融出口处，用甩丝机通过离心作用甩成丝；d、成丝得到的纤维进入收集器即得硅灰石纤维成品。进一步的，于原料中添加助熔剂，助熔剂占原料的重量比例为1%一5%，助熔剂为CaF2、B2O3和N2O中的至少一种。进一步的，所述步骤b中熔化时的熔化温度为1300~1800℃，被投入到电阻炉中时，被粉碎至10毫米以下。综上所述，本专利技术的一种硅灰石纤维制备方法通过将熔融的硅灰石或熔融的含硅质原料与石灰石吹拉成符合石棉用途要求指标的硅灰石长纤维，达到完...
【技术保护点】
一种硅灰石纤维制备方法，其特征在于，包括以下步骤：a、称取天然硅灰石990g、CaF210g，将这些原料通过磨机粉碎成10毫米以下的颗粒；b、将原料粉末投入电阻炉中，加热至1500‑1600℃熔融；c、在熔融出口处，用甩丝机通过离心作用甩成丝；d、成丝得到的纤维进入收集器即得硅灰石纤维成品。
【技术特征摘要】
1.一种硅灰石纤维制备方法，其特征在于，包括以下步骤：a、称取天然硅灰石990g、CaF210g，将这些原料通过磨机粉碎成10毫米以下的颗粒；b、将原料粉末投入电阻炉中，加热至1500-1600℃熔融；c、在熔融出口处，用甩丝机通过离心作用甩成丝；d、成丝得到的纤维进入收集器即得硅灰石纤维成品。2.根据权...
【专利技术属性】
技术研发人员：李兆源，
申请(专利权)人：江门市蓬江区亿艺广告设计工作室，
类型：发明
国别省市：广东,44