The present invention provides a method for removing calcium impurities in high purity magnesium nitrate, which comprises the following steps: (1) dissolved in nitric acid solution in the analysis of pure pure Magnesium Oxide analysis, after the completion of dissolution with hydrofluoric acid; (2) analysis of the use of pure Magnesium Oxide regulating PH = 7.5-8, 3-8min static 1-3H, stirring, filtering, concentrating a solution to the proportion of 1.4-1.42; (3) cooling to room temperature, separation and crystallization; the method after simple treatment can achieve effective removal efficiency, avoid duplication of concentration and crystallization of the treatment effect is good, the high pure grade reagent with magnesium nitrate standard, has a wide application prospect.
【技术实现步骤摘要】
一种高纯度硝酸镁中去除钙杂质的方法
本专利技术涉及一种杂质处理工艺，尤其是一种高纯度硝酸镁中去除钙杂质的方法。
技术介绍
高纯硝酸镁一般使用稀硝酸和分析纯氧化镁，经中和、结晶制备，分析纯氧化镁中，钙(Ca)的含量一般为0.02％，而使用高纯氧化镁，成本较高，因此通常制备高纯硝酸镁时，反复重结晶耗时长、能耗高、损耗大，经济性较差。因此，寻找一种方便有效的去除硝酸镁中含钙杂质的方法具有非常重要的生产实践意义。
技术实现思路
本专利技术所要解决的技术问题在于提供一种高纯度硝酸镁中去除钙杂质的方法。为解决上述技术问题，本专利技术的技术方案是：一种高纯度硝酸镁中去除钙杂质的方法，具体步骤为：(1)分析纯氧化镁溶于分析纯硝酸溶液中，溶解完成后加入氢氟酸；(2)使用分析纯氧化镁调节PH＝7.5-8，搅拌3-8min，静置1-3h，过滤，将溶液浓缩至比重1.4-1.42；(3)冷却至室温，分离结晶。优选的，上述高纯度硝酸镁中去除钙杂质的方法，具体步骤为：(1)分析纯氧化镁每400g，溶于2.5kg25％分析纯硝酸溶液(630g，以HNO3计)中，溶解完成后，加入氢氟酸1g(按HF计)；(2)使用分析纯氧化镁调节PH＝7.5-8，搅拌5min，静置2h，过滤，将溶液浓缩至比重1.4-1.42；(3)冷却至室温，分离结晶。上述高纯度硝酸镁中去除钙杂质的方法原理如下：MgF2,Ksp＝6.4×10-9，18℃溶解度87mg/L，折0.0087g/100ml；CaF2，Ksp＝2.7×10-11，18℃溶解度16mg/L，折0.0016g/100ml；两者在弱碱性条件下均难溶于水。因...
【技术保护点】
一种高纯度硝酸镁中去除钙杂质的方法，其特征在于：具体步骤为：(1)分析纯氧化镁溶于分析纯硝酸溶液中，溶解完成后加入氢氟酸；(2)使用分析纯氧化镁调节PH＝7.5‑8，搅拌3‑8min，静置1‑3h，过滤，将溶液浓缩至比重1.4‑1.42；(3)冷却至室温，分离结晶。
【技术特征摘要】
1.一种高纯度硝酸镁中去除钙杂质的方法，其特征在于：具体步骤为：(1)分析纯氧化镁溶于分析纯硝酸溶液中，溶解完成后加入氢氟酸；(2)使用分析纯氧化镁调节PH＝7.5-8，搅拌3-8min，静置1-3h，过滤，将溶液浓缩至比重1.4-1.42；(3)冷却至室温，分离结晶。2.根据权利要求1所述的高纯度硝酸镁中去...
【专利技术属性】
技术研发人员：林利成，苏学松，
申请(专利权)人：天津市科密欧化学试剂有限公司，
类型：发明
国别省市：天津,12