The present invention provides a novel nano titania composite fiber, consisting of silver nanoparticles, TiO2 nanoparticles and cellulose acetate, the preparation method comprises the following steps: 1) weigh silver nitrate and cellulose acetate, deionized water, 2 h 80 C water bath heating solution; 2) adding TiO2 nanoparticles, high speed stirring, until completely dissolved, was spinning solution; 3) will be loaded into the spinning liquid feeding system, using electrospinning processing for preparing nano titanium dioxide composite fiber. The novel nano titanium dioxide based composite fiber of the invention is a titanium dioxide based composite fiber with good performance, and has good antibacterial effect.
【技术实现步骤摘要】
新型纳米二氧化钛基复合纤维
本专利技术涉及一种新型纳米二氧化钛基复合纤维，属于化工材料
技术介绍
纳米二氧化钛是白色疏松粉末，屏蔽紫外线作用强，有良好的分散性和耐候性。可用于化妆品、功能纤维、塑料、涂料、油漆等领域，作为紫外线屏蔽剂，防止紫外线的侵害。也可用于高档汽车面漆，具有随角异色效应。纳米级二氧化钛，亦称钛白粉。直径在100纳米以下，产品外观为白色疏松粉末。具有抗线、抗菌、自洁净、抗老化性能，可用于化妆品、功能纤维、塑料、油墨、涂料、油漆、精细陶瓷等领域。纳米二氧化钛主要有两种结晶形态：锐钛型（Anatase）和金红石型（Rutile）。金红石型二氧化钛比锐钛型二氧化钛稳定而致密，有较高的硬度、密度、介电常数及折射率，其遮盖力和着色力也较高。而锐钛型二氧化钛在可见光短波部分的反射率比金红石型二氧化钛高，带蓝色色调，并且对紫外线的吸收能力比金红石型低，光催化活性比金红石型高。在一定条件下，锐钛型二氧化钛可转化为金红石型二氧化钛。纳米纤维是指直径处在纳米尺度范围(1～100nm)内的纤维，根据其组成成分可分为聚合物纳米纤维、无机纳米纤维及有机/无机复合纳米纤维。纳米纤维具有孔隙率高、比表面积大、长径比大、表面能和活性高、纤维精细程度和均一性高等特点，同时纳米纤维还具有纳米材料的一些特殊性质，如由量子尺寸效应和宏观量子隧道效应带来的特殊的电学、磁学、光学性质。纳米纤维主要应用在分离和过滤、生物及医学治疗、电池材料、聚合物增强、电子和光学设备和酶及催化作用等方面。随着纳米纤维材料在各领域应用技术的不断发展,纳米纤维的制备技术也得到了进一步开发与创新...
【技术保护点】
新型纳米二氧化钛基复合纤维，其特征在于，由银纳米粒子、TiO2纳米粒子和醋酸纤维素组成，其制备方法包括如下步骤：1）称取硝酸银和醋酸纤维素，加入去离子水，80℃水浴加热2 h 溶解；2）加入TiO2纳米粒子，高速搅拌分散，至完全溶解，得纺丝液；3）将纺丝液装入给料系统中，使用静电纺丝装置加工制备纳米二氧化钛基复合纤维。
【技术特征摘要】
1.新型纳米二氧化钛基复合纤维，其特征在于，由银纳米粒子、TiO2纳米粒子和醋酸纤维素组成，其制备方法包括如下步骤：1）称取硝酸银和醋酸纤维素，加入去离子水，80℃水浴加热2h溶解；2）加入TiO2纳米粒子，高速搅拌分散，至完全溶解，得纺...
【专利技术属性】
技术研发人员：田永圣，
申请(专利权)人：南通美铭锦纶有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。