The invention discloses a glass fiber reinforced polypropylene, which is composed of the following percentage by weight measurement components: 62 ~ 66%, polypropylene glass 28 ~ 32%, 4 ~ 6% compatilizers, 0.3 ~ 0.7% and 0.04 TiO2 lubricant to 0.08%. The present invention further optimized by polypropylene component, and add the right amount of nanometer titanium dioxide in the component, effectively solves the problem of glass fiber bundles into the group, do not need to increase the shear capacity of the extruder screw, ensure that the production process of mixture through the extruder die hole without obstacles, basically realize the production process fault, and the surface of the product is made of smooth appearance. On the other hand is a ton of product produces only 3 to 7 kg weight of the fragment, only about 1/10 of the existing technology.
【技术实现步骤摘要】
玻纤增强聚丙烯
本专利技术属于有机材料
,具体地讲,本专利技术涉及一种聚丙烯,特别是一种靠添加玻纤增强的聚丙烯。
技术介绍
聚丙烯是一种通用型工程塑料,自然状态下聚丙烯是无色或稍呈白色的蜡状固体,无味无毒。聚丙烯的密度仅为0.90~0.91g/cm3,抗拉强度、屈服强度均优于高密度聚乙烯,它具有良好的化学稳定性,且性价比高,是制作汽车、家电、蓄电池等产品构件的优选材料之一。为了进一步增强聚丙烯材质零部件的强度、低翘曲蠕变性和抗动态疲劳等性能,生产厂家通常在聚丙烯中添加适量玻纤,以及辅料类的相容剂和润滑剂。尽管现有技术实施简便,增强效果明显。但是,在生产过程中因添加的玻纤难以剪断,过长的玻纤造成混料不均,一方面导致成团或成束的玻纤内部得不到树脂有效湿润,另一方面成团成束的玻纤易构成挤出机模孔堵塞或不畅通,由此造成断条过多或产品粗糙。在现有技术条件下,提高挤出机的剪切能力,虽然可以有效剪短玻纤,可是玻纤被剪得过短,又达不到增强聚丙烯的目的。
技术实现思路
本专利技术主要针对现有技术不足,提出一种组分配置合理、混料均匀、挤出顺畅、产品表面光滑、断条少的玻纤增强聚丙烯。本专利技术通过下述技术方案实现技术目标。玻纤增强聚丙烯,它由下列按重量百分比计量的组分构成:聚丙烯62~66%、玻纤28~32%、相容剂4.0~6.0%、润滑剂0.3~0.7%和二氧化钛0.04~0.08%。作为进一步改进方案,所述聚丙烯为共聚聚丙烯与均聚聚丙烯的混合物,其中按重量百分比计量的共聚聚丙烯为76~79%,其余为均聚聚丙烯。作为进一步改进方案,所述相容剂为马来酸酐或丙烯酸缩水甘油酯。作 ...
【技术保护点】
一种玻纤增强聚丙烯,其特征在于:它由下列按重量百分比计量的组分构成:聚丙烯62~66%、玻纤28~32%、相容剂4.0~6.0%、润滑剂0.3~0.7%和二氧化钛0.04~0.08%。
【技术特征摘要】
1.一种玻纤增强聚丙烯,其特征在于:它由下列按重量百分比计量的组分构成:聚丙烯62~66%、玻纤28~32%、相容剂4.0~6.0%、润滑剂0.3~0.7%和二氧化钛0.04~0.08%。2.根据权利要求1所述的玻纤增强聚丙烯,其特征在于:所述聚丙烯为共聚聚丙烯与均聚聚丙烯的混合物,其中按重量百分比计量的共聚聚丙烯为76~79%,其余为...
【专利技术属性】
技术研发人员:蒋靖,夏玲玲,张云云,
申请(专利权)人:双登集团股份有限公司,
类型:发明
国别省市:江苏,32