The invention relates to a foamed organic silicon material and a preparation method thereof, belonging to the technical field of organosilicon. Foamed silicone material of the invention comprises the following raw materials according to the weight: 80 portions, 60 hydroxy silicone oil vinyl silicone oil 5 10, 10 20 hydrogen containing silicone oil, lauric acid two two butyl tin 1 2 copies, 5 copies of 3 quaternary ammonium alkali, nanometer calcium carbonate 5 10. The silicone foam material is prepared by using hydroxy silicone oil, vinyl silicone oil and hydrogen containing silicone oil as main raw materials. The foamed silicone material has excellent comprehensive mechanical properties, and has uniform bubble, fine density and good elasticity.
【技术实现步骤摘要】
本专利技术涉及一种有机硅材料及其制备方法,更具体地说,本专利技术涉及一种发泡有机硅材料及其制备方法,属于有机硅
技术介绍
软质泡沫材料是泡沫塑料的一大类品种,因柔软、弹性好,广泛应用于工业、农业、交通运输、军事、建筑及日用品等领域。由于其结构的特殊性,故具有许多其它材料所不能同时具备的优异性能,如卓越的耐高温与耐低温性、优良的电绝缘与化学稳定性、良好的耐老化性、突出的表面活性、憎水防潮和生理惰性等。通常作为阻尼、隔音、减震、电绝缘封装等材料应用于航空航天领域作为航天器、火箭等的轻质、耐高温、抗湿材料等。现有软质泡沫材料机械性能较差,且泡孔不均匀,细密和弹性也较差。
技术实现思路
本专利技术旨在解决现有技术中的问题,提供一种发泡有机硅材料,该发泡有机硅材料具有优异综合机械性能,且泡孔均匀,细密和弹性良好。为了实现上述专利技术目的,其具体的技术方案如下:一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油60-80份乙烯基硅油5-10份含氢硅油10-20份二月桂酸二丁基锡1-2份季氨碱3-5份纳米级碳酸钙5-10份。优选的,一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油66份乙烯基硅油9份含氢硅油12份二月桂酸二丁基锡1.2份季氨碱4.6份纳米级碳酸钙8份。一种发泡有机硅材料的制备方法,其特征在于:包括以下工艺步骤:A、于一个三口反应器内加入羟基硅油和二月桂酸二丁基锡;于130-150℃下预聚1-3h,然后在160-180℃下预聚1-3h;B、加入乙烯基硅油、纳米级碳酸钙和季氨碱,搅拌混合;加入含氢硅油,快速搅 ...
【技术保护点】
一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油 60‑80份乙烯基硅油 5‑10份含氢硅油 10‑20份二月桂酸二丁基锡 1‑2份季氨碱 3‑5份纳米级碳酸钙 5‑10份。
【技术特征摘要】
1.一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油60-80份乙烯基硅油5-10份含氢硅油10-20份二月桂酸二丁基锡1-2份季氨碱3-5份纳米级碳酸钙5-10份。2.根据权利要求1所述的一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油66份乙烯基硅油9份含氢硅油12份二月桂酸二丁基锡1.2份季氨碱4.6份纳米级碳酸钙8份。3.根据权利要求1或2所述的一种发泡有机硅材料的制备方法,其特征在于:包括以下工艺步骤:A、于一个三口反应器内加入羟基硅油和二月桂酸二丁基锡;于130-150...
【专利技术属性】
技术研发人员:赵奕,王凤德,高川,刘咏梅,王煦怡,
申请(专利权)人:中蓝晨光化工研究设计院有限公司,
类型:发明
国别省市:四川;51