The invention discloses a floor seam cracking of high toughness polyurethane sealant for building, which is composed of the following parts by weight of raw materials: 40 50 mica powder, gypsum whisker 10 5, 20 40 lignin, solid content of EVA emulsion 40 50% 3 5, solid content of soy protein emulsion 20 30% 3 5, 100 120 polyoxypropylene glycol, isophorone diisocyanate 30 60, two two 0.5 lauric acid butyl tin 1, aminopropyltriethoxysilane 3 5, 1.5 2.5 TEOS, adjacent benzene two formic acid two - 40 60, cellulose acetate butyrate 0.5 1. The present invention polyurethane building sealant has excellent weatherability, adhesion properties and high stability, good durability, long service life, and high toughness and anti cracking characteristics, suitable for the use of seam floor.
【技术实现步骤摘要】
本专利技术涉及密封胶
，尤其涉及一种地板拼缝高韧性抗裂聚氨酯建筑密封胶及其制备方法。
技术介绍
密封胶是指引随密封面形状而变形，不易流淌，有一定粘结性的密封材料，是用来填充构形间隙、以起到密封作用的胶粘剂，具有防泄漏、防水、防振动及隔音、隔热等作用。建筑的外围护、室内装饰装修、窗结构以及其它形式的围护和装饰结构是由单元组成，而单元之间产生的接缝绝大多数需要建筑用密封胶来密封填充。合理的建筑用密封胶选材和建筑密封的正确施工是保证建筑接缝密封成功必不可少的环节。聚氨酯密封胶具有设备、工艺简单、无污染、粘接强度高、快速固化、施工方便等优点，在建筑领域得到广泛的应用。然而，现有的聚氨酯密封胶的耐候性较差，容易受紫外光老化，影响了其性能和使用寿命。CN201310164862公布了一种含木质素的聚氨酯密封胶，通过木质素替代三元醇合成聚氨酯密封胶，有效提高材料的耐光老化性能。然而在聚氨酯密封胶中引入木质素增加了密封胶的吸潮性，从而影响密封胶的稳定性。因此，有必要对其进行改进。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷，提供一种具有优良耐候性以及高稳定性的地板...
【技术保护点】
一种地板拼缝高韧性抗裂聚氨酯建筑密封胶，其特征在于，其是由下述重量份的原料制得：云母粉40‑50，石膏晶须5‑10，木质素20‑40，固含量为40‑50%的EVA乳液3‑5，固含量为20‑30%的大豆蛋白乳液3‑5，聚氧化丙烯二醇100‑120，异佛尔酮二异氰酸酯30‑60，二月桂酸二丁基锡0.5‑1，氨丙基三乙氧基硅烷3‑5，正硅酸乙酯1.5‑2.5，邻苯二甲酸二辛酯40‑60，醋酸丁酸纤维素0.5‑1；所述聚氧化丙烯二醇的数均分子量为2000‑6000；所述木质素为玉米秸秆木质素。
【技术特征摘要】
1.一种地板拼缝高韧性抗裂聚氨酯建筑密封胶，其特征在于，其是由下述重量份的原料制得：云母粉40-50，石膏晶须5-10，木质素20-40，固含量为40-50%的EVA乳液3-5，固含量为20-30%的大豆蛋白乳液3-5，聚氧化丙烯二醇100-120，异佛尔酮二异氰酸酯30-60，二月桂酸二丁基锡0.5-1，氨丙基三乙氧基硅烷3-5，正硅酸乙酯1.5-2.5，邻苯二甲酸二辛酯40-60，醋酸丁酸纤维素0.5-1；所述聚氧化丙烯二醇的数均分子量为2000-6000；所述木质素为玉米秸秆木质素。2.根据权利要求1所述的一种地板拼缝高韧性抗裂聚氨酯建筑密封胶的制备方法，其特征在于，包括以下步骤：（1）...
【专利技术属性】
技术研发人员：刘晓朋，
申请(专利权)人：天长市永泰密封材料有限公司，
类型：发明
国别省市：安徽;34