The invention relates to a high toughness epoxy resin and a preparation method thereof, which belongs to the technical field of epoxy resin. Epoxy resin of the invention comprises the following according to the weight of raw materials: bisphenol A epoxy resin E 44 30 45, E 51 20 30, 12 20 30 E, styrene maleic anhydride copolymer 30 50 copies, 3 copies of 2 2-methylimidazole. The invention comprises a plurality of epoxy resin as matrix resin, styrene maleic anhydride copolymer as curing agent, methyl imidazole as catalyst, starting from molecular design, the use of functional groups anhydride styrene maleic anhydride copolymer in the curing of epoxy resin, epoxy resin with good comprehensive properties and high toughness was prepared.
【技术实现步骤摘要】
本专利技术涉及一种环氧树脂及其制备方法,更具体地说,本专利技术涉及一种高韧性环氧树脂及其制备方法,属于环氧树脂
技术介绍
酸酐固化环氧树脂体系具有优良的力学和电气性能以及高温稳定性,在电器行业具有广泛的应用。目前国内对酸酐类固化剂的研究基本都局限于对低分子的酸酐,由于低分子的酸酐的毒性及其对环境的污染,人们转而使用高分子量的苯乙烯-马来酸酐共聚物作为环氧树脂的固化剂。苯乙烯-马来酸酐共聚物中的马来酸酐链段在环氧树脂聚合物材料的分子设计中有重要作用,可以根据需要设计出新的功能化聚合物。此外,采用苯乙烯-马来酸酐共聚物固化的环氧树脂具有优良的耐热性和电性能。现有环氧树脂综合性能不佳,特别是韧性需要提高。
技术实现思路
本专利技术旨在解决现有技术中的环氧树脂综合性能不佳,特别是韧性需要提高的问题,提供一种高韧性环氧树脂,该环氧树脂的综合性能较好,特别是具有高韧性的特点。为了实现上述专利技术目的,其具体的技术方案如下:一种高韧性环氧树脂,其特征在于:包括以下按照重量份数计的原料:双酚A型环氧树脂E-4430-45份E-5120-30份E-1220-30份苯乙烯-马来酸酐共聚物30-50份甲基咪唑2-3份。一种高韧性环氧树脂的制备方法,其特征在于:包括以下工艺步骤:A、按配方要求称取各反应组分双酚A型环氧树脂E-44、E-51、E-12、苯乙烯-马来酸酐共聚物和甲基咪唑于研钵中研磨并于烧杯中充分混合均匀;B、将混合物倒入模具中,于80-90℃固化2-4h;C、然后在100-120℃固化2-3h;再在130-140℃固化2-5h;最后在160-170℃固化4- ...
【技术保护点】
一种高韧性环氧树脂,其特征在于:包括以下按照重量份数计的原料:双酚A型环氧树脂E‑44 30‑45份E‑51 20‑30份E‑12 20‑30份苯乙烯‑马来酸酐共聚物 30‑50份甲基咪唑 2‑3份。
【技术特征摘要】
1.一种高韧性环氧树脂,其特征在于:包括以下按照重量份数计的原料:双酚A型环氧树脂E-4430-45份E-5120-30份E-1220-30份苯乙烯-马来酸酐共聚物30-50份甲基咪唑2-3份。2.根据权利要求1所述的一种高韧性环氧树脂的制备方法,其特征在于:包括以下工艺步骤:A、按配方要...
【专利技术属性】
技术研发人员:赵奕,王凤德,高川,刘咏梅,王煦怡,
申请(专利权)人:中蓝晨光化工研究设计院有限公司,
类型:发明
国别省市:四川;51