一种对赤泥进行磁化焙烧‑磁选的方法技术
A method for separation of red mud magnetization roasting
The invention discloses a method for magnetic roasting magnetic separation of red mud, the method comprises the following steps: the red mud drying, crushing and grinding to a particle size below 0.25mm, with a certain amount of alkali lignin reduction agent are evenly mixed; the red mud and the alkali lignin reduction mixture agent microwave reaction device in the microwave magnetic roasting, obtained calcine; the obtained calcine natural cooling after ball milling, the milled pulp magnetic separation in magnetic separator, iron concentrate. The invention adopts alkali lignin as reducing agent and microwave as heating source, and has the advantages of low cost, mild heating condition, rapid heating speed, selective heating, high safety and environmental protection.
【技术实现步骤摘要】
本专利技术涉及赤泥回收
，更具体涉及一种对赤泥进行磁化焙烧-磁选的方法。
技术介绍
赤泥为氧化铝生产中排出的红褐色粉泥状的固体废渣，一般平均每生产1吨氧化铝会产生1～2吨以三氧化二铁等不溶物为主的赤泥。目前，国内外对赤泥的处理方式主要为筑坝堆存，我国是世界第四大氧化铝生产国，累积赤泥堆存量已高达2亿多吨，不仅占用大量的土地，消耗大量的筑坝基建和维护费用，造成了资源的二次浪费，同时也带来了严重的环境污染问题，严重的制约了铝工业的可持续发展。对现存赤泥进行有效处理，开发赤泥的可行性利用新技术，促进资源的二次利用，具有重大的经济和社会意义。赤泥中含有大量的铁元素，主要以三氧化二铁的形式存在，从赤泥中高效回收铁不仅有利于缓解我国钢铁行业对铁矿需求的压力，又可以有效的实现资源的回收利用，是近年来赤泥综合利用的研究热点，具有重大的现实意义。磁选是回收铁的重要手段，然而由于赤泥中含有的赤铁矿磁性相对较弱，仅用物理选矿技术难以达到很好的回收效果。美国专利文件US2015203362(A1)公开了一种从铝土矿渣(赤泥)中回收磁铁矿的方法，该方法首先将赤泥中和、干燥后，采用C...
【技术保护点】
一种对赤泥进行磁化焙烧‑磁选的方法，其特征在于，该方法包括如下步骤：(1)称取赤泥，将赤泥烘干、破碎、磨矿至粒度为0.25mm以下，与一定量的碱木质素还原剂均匀混合；(2)将赤泥与碱木质素还原剂的混合物料加入微波反应装置内，进行微波加热磁化焙烧，得到焙砂；(3)将得到的焙砂自然冷却后进行球磨，将球磨矿浆在磁选机中进行磁选，得到铁精矿。
【技术特征摘要】
1.一种对赤泥进行磁化焙烧-磁选的方法，其特征在于，该方法包括如下步骤：(1)称取赤泥，将赤泥烘干、破碎、磨矿至粒度为0.25mm以下，与一定量的碱木质素还原剂均匀混合；(2)将赤泥与碱木质素还原剂的混合物料加入微波反应装置内，进行微波加热磁化焙烧，得到焙砂；(3)将得到的焙砂自然冷却后进行球磨，将球磨矿浆在磁选机中进行磁选，得到铁精矿。2.根据权利要求1所述的对赤泥进行磁化焙烧-磁选的方法，其特征在于，所述的赤泥为氧化铝工业所产生的废渣，其铁质量品位>10％。3.根据权利要求1所述的对赤泥进行磁化焙烧-磁选的方法，其特征在于，...
【专利技术属性】
技术研发人员：钟宏，武芳芳，王帅，曹占芳，刘广义，
申请(专利权)人：中南大学，
类型：发明
国别省市：湖南;43