一种仿石抛光砖及其生产方法技术

一种仿石抛光砖及其生产方法，其特征在于由主要含有ＳｉＯ↓［２］、Ａｌ↓［２］Ｏ↓［３］、ＭｇＯ、Ｋ↓［２］Ｏ、Ｎａ↓［２］Ｏ的透明配方粉料及传统陶瓷粉料经多管布料、瓷砖坯体成型、干燥、烧成、抛光制成，其中透明配方粉料中ＳｉＯ↓［２］的含量为６６－７５％ｗｔ，Ａｌ↓［２］Ｏ↓［３］的含量为１６－２５％ｗｔ，ＭｇＯ的含量为０．６－２．５％ｗｔ，Ｋ↓［２］Ｏ的含量为０．５－２．５％ｗｔ，Ｎａ↓［２］Ｏ的含量为４．５－１０％ｗｔ，透明配方粉料的含量占９０％－５０％ｗｔ。本发明专利技术与已有技术相比，所制造出来的瓷砖表面图案具有天然石材所具有的玉石般质感的、立体效果的优点。

Stone imitation polishing brick and production method thereof

An imitation stone polished brick and its production method, characterized by containing mainly SiO: 2, Al: 2 O: 3, MgO, K: 2, O: Na 2 O transparent formula powder and traditional ceramic powder by multi cloth, porcelain body forming, drying, sintering, polishing materials, the content of transparent powder in SiO formula: 2 to 66 75%wt, the content of Al decreases 2 O: 3 to 16 25%wt, the content of MgO is 0.6 2.5%wt, 2 O content is 0.5, down K 2.5%wt, 2 O Na content: the 4.5 - 10%wt, the content of transparent formula powder for 90%50%wt. Compared with the prior art, the surface pattern of the ceramic tile produced by the invention has the advantages of jade like texture and stereoscopic effect of the natural stone.

【技术实现步骤摘要】

本专利技术涉及一种瓷砖及其生产方法。
技术介绍
现有的抛光砖是采用传统配方作为基础浆加色制粉后，经压制成型为瓷砖坯体，然后经干燥、烧成、抛光而成。采用传统配方作为基础浆加色制粉虽然经过特定的布料工艺可生产出表面图案类似天然石材纹理的抛光砖，但抛光砖的表面图案与天然石材相比，缺乏立体效果，质感较差，缺乏玉石感觉，没有天然石材立体的、玉石般的那种天然效果。
技术实现思路
本专利技术的专利技术目的在于提供一种所制造出来的瓷砖表面图案具有天然石材所具有的玉石般质感的、立体效果的仿石抛光砖及其生产方法。本专利技术的仿石抛光砖是这样实现的，由主要含有SiO2、Al2O3、MgO、K2O、Na2O的透明配方粉料及传统陶瓷粉料经多管布料、瓷砖坯体成型、干燥、烧成、抛光制成，其中透明配方粉料中SiO2的含量为66-75％wt，Al2O3的含量为16-25％wt，MgO的含量为0.6-2.5％wt，K2O的含量为0.5-2.5％wt，Na2O的含量为4.5-10％wt，透明配方粉料的含量占90％-50％wt。SiO2、是Al2O3制成玻璃体的主要成分，Na2O的作用是提升玻璃体的透明程度，Na2O在透明配本文档来自技高网...

【技术保护点】
一种仿石抛光砖，其特征在于由主要含有ＳｉＯ２、Ａｌ２Ｏ３、ＭｇＯ、Ｋ２Ｏ、Ｎａ２Ｏ的透明配方粉料及传统陶瓷粉料经多管布料、瓷砖坯体成型、干燥、烧成、抛光制成，其中透明配方粉料中ＳｉＯ２的含量为６６－７５％ｗｔ，Ａｌ２Ｏ３的含量为１６－２５％ｗｔ，ＭｇＯ的含量为０．６－２．５％ｗｔ，Ｋ２Ｏ的含量为０．５－２．５％ｗｔ，Ｎａ２Ｏ的含量为４．５－１０％ｗｔ，透明配方粉料的含量占９０％－５０％ｗｔ。

【技术特征摘要】

【专利技术属性】
技术研发人员：林家生，文迪田，刘汉津，魏明东，贾平，刘建辉，黄金宝，周玉球，汪海应，杨文华，
申请(专利权)人：广东博华陶瓷有限公司，
类型：发明
国别省市：44[中国|广东]