Environment friendly energy-saving building insulation material convenient for construction. The environmental protection energy-saving housing insulation materials by different weight of sepiolite, fibrous brucite, high strength gypsum, 425 cement, adhesive, foaming agent and water repellent perlite mixing and become, the appearance of a dry bulk fiber. The water wall material and mixing can be directly put on the housing to a certain thickness of inner wall and roof insulation, has the characteristics of energy saving and environmental protection, waterproof construction is simple and fast, suitable for all kinds of insulation of buildings, achieve high efficiency and energy saving effect.
【技术实现步骤摘要】
本专利技术涉及一种新型的房屋保温材料,尤其适用于各种房屋建筑结构的内、外墙保温。
技术介绍
目前,我国在房屋建筑节能保温方面的应用还并不多,大部分房屋建筑并未采用保温材料,而已有的保温材料和技术也多从建筑外墙入手,一般为板材保温材料,在施工时需要添加粘结剂或钢筋网架等固定设施,造成施工成本高、容易脱落、表面极易产生裂纹、保温性能差、防水不好等现象。
技术实现思路
为克服现有技术的不足,本专利技术提供一种环保型节能房屋保温材料。该房屋保温材料应用后不仅施工方便简单、降低施工成本、缩短施工周期,而且保温效果好,无毒、无味、无污染,生产过程简单,且与建筑材料同属硅酸盐系列,同建筑结构天然浑成,同步老化,寿命长久。本专利技术由40公斤海泡石,40公斤纤维水镁石,70公斤高强度石膏,10公斤425号水泥,10公斤粘合剂,10公斤发泡剂,90公斤憎水珍珠岩混合搅拌而成,外观呈干粉纤维散状。施工时,将本房屋保温材料加适量水搅拌为类似水泥砂浆的糊状,以一定厚度采用常规的瓦工、抹工工法直接抹在房屋建筑的外墙或内墙,干后在其表面再抹一层水泥砂浆固化即可。本专利技术由于只需要将各种原料按比例搅拌均匀即可,所以加工十分方便,且加工成本低廉。由于采用的原料配方均为无毒无污染的环保材料,所以使得本专利技术环保无害。由于本专利技术采用高强度石膏和憎水珍珠岩,使本专利技术具有一定的防水效果且强度高。本专利技术的导热系数为0.056W/m.K(22℃),体积收缩率为2.1%,使得本专利技术具有高效的保温节能效果,体积收缩率极低,且固化快、抗击强度高、粘结强度大、不粉化、不龟裂、不空鼓、不脱 ...
【技术保护点】
一种环保型节能房屋保温材料,由40公斤海泡石,40公斤纤维水镁石,70公斤高强度石膏,10公斤425号水泥,10公斤粘合剂,10公斤发泡剂,90公斤憎水珍珠岩混合搅拌而成,外观呈干粉纤维散状。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。