本发明专利技术涉及一种轻骨料砼模壳墙体构件材料及其生产工艺，由分别配制的外表面层和内层的双组分配料，经同步二次布料制作而成模壳墙体构件；外表面层材料的重量配比如下：水泥：３３～３７．６５％，轻集料：３４～３７％，掺和料：９～１１．５％，辅料Ａ：１．０～１．５％，辅料Ｂ：０．１０～０．１５％，外加剂：０．２５～０．４５％，水：１８～２２．６５％；构件内层材料的重量配比如下：水泥：５３～５８．０％，超轻集料：３．１～３．５３％，掺和料：１０．５～１２％，辅料Ｃ：１．２～２．０％，辅料Ｂ：０．０５～０．０８％，外加剂：０．１５～０．２０％，水：２７～３２％；它是强度高、质量轻、施工简便、取材广泛、造价低、结构合理、性能良好的模壳墙体构件材料。

Lightweight aggregate concrete mould shell wall component material and production process thereof

The invention relates to a lightweight concrete shell wall material and its production process, by the two ingredients were prepared on the outer surface and inner layer, the synchronization of two fabrics made of shell wall components; the outer surface layer of material weight ratio is as follows: cement: 33 ~ 37.65%, light aggregate: 34 ~ 37%, 9 ~ 11.5%, admixture: accessories accessories A:1.0 ~ 1.5%, B:0.10 ~ 0.15%, 0.25 ~ 0.45%, admixture: water: 18 ~ 22.65%; the inner component material weight ratio is as follows: cement: 53 ~ 58%, super light aggregate: 3.1 ~ 3.53%, 10.5 ~ 12%, admixture: accessories C:1.2 ~ 2%, B:0.05 ~ 0.08 accessories %, additive: 0.15 ~ 0.20%, water: 27 ~ 32%; it is of high strength, light weight, convenient construction, material shell wall components wide material, low cost, reasonable structure, good performance.

【技术实现步骤摘要】

【技术保护点】
一种轻骨料砼模壳墙体构件材料，其特征在于：由分别配制的外表面层和内层的双组分配料，经同步二次布料制作而成模壳墙体构件；（１）外表面层材料的重量配比如下：水泥：３３～３７．６５％，轻集料：３４～３７％，掺和料：９～１１．５％， 辅料Ａ：１．０～１．５％，辅料Ｂ：０．１０～０．１５％，外加剂：０．２５～０．４５％，水：１８～２２．６５％；轻集料：页岩陶粒、粉煤灰陶粒、浮石、多孔火山岩、自燃煤矸石、膨胀珍珠岩、漂珠其中之一至二种；掺和料：粉煤灰、矿渣细粉、石英 粉、火山灰等无机矿物细粉料之一至二种；辅料Ａ：乙酸乙烯共聚物；辅料Ｂ：聚丙烯纤维或聚酯纤维；外加剂：萘系高效减水剂；（２）构件内层材料的重量配比如下：水泥：５３～５８．０％，超轻集料：３．１～３．５３％，掺和料：１０．５～１ ２％，辅料Ｃ：１．２～２．０％，辅料Ｂ：０．０５～０．０８％，外加剂：０．１５～０．２０％，水：２７～３２％；超轻集料：膨胀珍珠岩、漂珠、聚苯乙烯或其它泡沫塑料之一至二种；掺和料：粉煤灰、矿渣细粉、石英粉、火山灰等活性或非活性无机矿 物细粉料之一至二种；辅料Ｃ：聚乙烯醇；辅料Ｂ：聚丙烯纤维或聚酯纤维；外加剂：萘系高效减水剂。...

【技术特征摘要】

【专利技术属性】
技术研发人员：万国良，刘泳霞，
申请(专利权)人：刘泳霞，
类型：发明
国别省市：13[中国|河北]