The invention relates to ceramic production technology, in particular to liquid phase sintering production technology of silicon carbide ceramics. The invention provides a new technical scheme. The technical proposal provided by the invention can improve the utilization rate of the related production equipment, improve the production efficiency of the silicon carbide ceramic, and reduce the energy consumption in the production process. In the technical scheme of the invention, the raw materials including silicon carbide powder, yttrium oxide, alumina and binder, by mixing, molding, curing and high temperature sintering process, the formation of silicon carbide ceramic products, which is characterized in that the technical scheme comprises the following steps: A. yttria and alumina two kinds of raw materials were mixed, the ball milling, generating flux prefabricated material by mechanical chemical method; B. flux prefabricated material and silicon carbide powder and binder are mixed by molding, curing and high temperature sintering process, the formation of silicon carbide ceramic products.
【技术实现步骤摘要】
本专利技术涉及陶瓷生产技术，特别是碳化硅陶瓷的液相烧结生产技术。本专利技术提供一种新的技术方案。本专利技术提供的技术方案有助于提高相关生产设备的利用率，提高碳化硅陶瓷的生产效率，减少生产过程中的能耗。碳化硅陶瓷材料具有高温强度大、高温抗氧化性强、耐磨损性能好、热稳定性佳、热膨胀系数小、热导率大、硬度高、抗热震和耐化学腐蚀等优良特性，在汽车、机械化工、环境保护、空间技术、信息电子、能源等领域有着日益广泛的应用，已经成为一种在很多工业领域性能优异的其他材料不可替代的结构陶瓷。在汽车工业中，为了提高发动机的热效率，充分利用能源，降低燃料消耗，减少大气污染，希望发动机的工作温度高于1200度(据计算，发动机的工作温度由1100度提高到1370度时，热效率可增加30％)。碳化硅陶瓷因所具有的高温强度，较低的热膨胀系数，较高的导热系数和较好的抗热冲击性而被认为是使用温度超过1200度的最有前途的候选材料。拥有先进陶瓷技术的国家如美国、德国和日本已研发出采用碳化硅陶瓷的发动机零部件如发动机定子、转子、燃烧器及涡形管并取得了良好的使用效果，目前正致力于全陶瓷发动机的开发研究...
【技术保护点】
液相烧结碳化硅陶瓷的一种生产工艺，所用原料包括碳化硅粉、氧化钇、氧化铝以及结合剂，经混料、模压定型、固化、高温烧结等过程，形成碳化硅陶瓷产品，其特征在于，该生产工艺包括以下步骤：ａ，将氧化钇和氧化铝两种原料混合，进行球磨，利用机械化 学法生成助熔剂预制料；ｂ，将助熔剂预制料与碳化硅粉以及结合剂等进行混合，经模压定型、固化、高温烧结等过程，形成碳化硅陶瓷产品。
【技术特征摘要】
【专利技术属性】
技术研发人员：李榕生，水淼，陈红兵，干宁，宋岳，王霞，胡乾，林安，任元龙，
申请(专利权)人：宁波大学，
类型：发明
国别省市：97[中国|宁波]