本发明专利技术涉及陶瓷，是关于碳化硅陶瓷，特别是一种嵌入物包括碳化硅晶须的多成份碳化硅陶瓷。本发明专利技术的特点，是利用多种形貌的氧化铝颗粒替换掉一部分的相对昂贵的并且相对难于混料的碳化硅晶须，本发明专利技术的方案是结合利用所述多种形貌的氧化铝颗粒与碳化硅晶须一起对碳化硅陶瓷进行组合增韧，所述氧化铝嵌入颗粒原料相对廉价，并且，所述氧化铝嵌入颗粒原料易于与其它物料均匀混合。

An embedded composite silicon carbide ceramic comprising a silicon carbide whisker

The present invention relates to ceramics, and is a composition of silicon carbide ceramic, in particular an embedded silicon carbide ceramic composition including silicon carbide whiskers. The characteristic of this invention is to use a variety of alumina particles, morphology and replace part of the relatively expensive and is difficult to be mixed with silicon carbide whiskers, the scheme of the invention is combined with alumina particles and the silicon carbide whiskers of various morphologies of silicon carbide ceramics in combination with toughening, the alumina particles embedded materials are relatively inexpensive, also, the alumina particle materials and other materials are uniformly mixed easily.

【技术实现步骤摘要】
一种嵌入物包括碳化硅晶须的多成份碳化硅陶瓷本专利技术涉及一种陶瓷，是关于碳化硅陶瓷，特别是一种嵌入物包括碳化硅 晶须的多成份碳化硅陶瓷。目前报道的增韧碳化硅陶瓷，多是含有碳化硅晶须或炭纤维的增韧碳化硅 陶瓷。有关含有碳化硅晶须的增韧碳化硅陶瓷的报道参见田杰谟等专利技术(设计)，清华大学申请，申请号为CN91101684. 8的专利申请案"晶须增韧强化碳 陶瓷复合材料"；以及，阿历山大* J *派齐克专利技术(设计)，唐化学原料公司 申请，申请号为CN90110427.2的专利申请案"碳化硅晶须增强陶瓷复合材料 及其制造方法"；以及，成来飞、张立同、徐永东、刘永胜、李镇、王晓明等发 明(设计)，中国西北工业大学申请，申请号为CN200410026337.6的专利申请 案"一种晶须和颗粒增韧陶瓷基复合材料制备方法"。有关含有炭纤维的增韧 碳化硅陶瓷的报道参见耿浩然等专利技术(设计)，济南大学申请，申请号为 CN03138926.0的专利申请案"一种制备碳纤维增强碳化硅复合材料的装置及 工艺"。碳化硅陶瓷材料具有高温强度大、高温抗氧化性强、耐磨损性能好、热稳 定性佳、热膨胀系数小、热导率大、本文档来自技高网...

【技术保护点】
一种嵌入物包括碳化硅晶须的多成份碳化硅陶瓷，其组成如下：（１）碳化硅晶粒５０％～９２％（重量）（２）碳化硅晶须２％～１０％（重量）（３）片状氧化铝嵌入颗粒２％～１０％（重量）（４）棒状氧化铝嵌入颗粒２％～１０％（重量）（５）球状氧化铝嵌入颗粒２％～８％（重量）（６）碳化硼或钇铝石榴石０％～１２％（重量）。