一种嵌入物包括纤维、晶须的多成份碳化硅陶瓷制造技术

本发明专利技术涉及陶瓷，是关于碳化硅陶瓷，特别是一种嵌入物包括纤维、晶须的多成份碳化硅陶瓷。本发明专利技术的特点，是利用碳化硅晶须以及炭纤维的增韧强势，在结合使用碳化硅晶须以及炭纤维的同时，引入多种形貌的氧化铝颗粒，与碳化硅晶须以及炭纤维一起对碳化硅陶瓷进行组合增韧；其中，所述多种形貌的氧化铝颗粒相对廉价，并且易于与其它物料均匀混合；本发明专利技术的方案减小了对于相对难于分散的碳化硅晶须以及炭纤维的依赖程度，并弱化了混料不均可能带来的负面影响。

An embedded composite silicon carbide ceramic comprising fibers and whiskers

The present invention relates to ceramics, and is a multi component silicon carbide ceramic used for silicon carbide ceramics, in particular an insert including fibers and whiskers. The characteristic of this invention, is the use of toughened silicon carbide whisker and carbon fiber strength, used in combination with silicon carbide whisker and carbon fiber at the same time, the introduction of a variety of morphology of alumina particles, and silicon carbide whisker and carbon fiber on silicon carbide ceramic combined toughening; alumina particles in the various morphologies of relatively cheap, easy and uniform mixed with other materials; the scheme of the invention has less dependence on difficult to disperse silicon carbide whisker and carbon fiber, and weaken the negative effect caused by inhomogeneous material mixing.

【技术实现步骤摘要】
一种嵌入物包括纤维、晶须的多成份碳化硅陶瓷本专利技术涉及一种陶瓷，是关于碳化硅陶瓷，特别是一种嵌入物包括纤维、 晶须的多成份碳化硅陶瓷。目前报道的增韧碳化硅陶瓷，多是含有碳化硅晶须或炭纤维的增韧碳化硅 陶瓷。有关含有碳化硅晶须的增韧碳化硅陶瓷的报道参见田杰谟等专利技术(设 计)，清华大学申请，申请号为CN91101684.8的专利申请案"晶须增韧强化碳 陶瓷复合材料"；以及，阿历山大，J ，派齐克专利技术(设计)，唐化学原料公司 申请，申请号为CN90110427.2的专利申请案"碳化硅晶须增强陶瓷复合材料 及其制造方法"；以及，成来飞、张立同、徐永东、刘永胜、李镇、王晓明等发 明(设计)，中国西北工业大学申请，申请号为CN200410026337.6的专利申请 案"一种晶须和颗粒增韧陶瓷基复合材料制备方法"。有关含有炭纤维的增韧 碳化硅陶瓷的报道参见耿浩然等专利技术(设计)，济南大学申请，申请号为 CN03138926.0的专利申请案"一种制备碳纤维增强碳化硅复合材料的装置及 工艺"。碳化硅陶瓷材料具有高温强度大、高温抗氧化性强、耐磨损性能好、热稳 定性佳、热膨胀系数小、热导率大、硬本文档来自技高网...

【技术保护点】
一种嵌入物包括纤维、晶须的多成份碳化硅陶瓷，其组成如下：（１）碳化硅晶粒４０％～９０％（重量）（２）碳化硅晶须２％～１０％（重量）（３）炭纤维２％～１０％（重量）（４）片状氧化铝嵌入颗粒２％～１０％（重量）（５）棒状氧化铝嵌入颗粒２％～１０％（重量）（６）球状氧化铝嵌入颗粒２％～８％（重量）（７）碳化硼或钇铝石榴石０％～１２％（重量）。

【技术特征摘要】

【专利技术属性】
技术研发人员：李榕生，水淼，王霞，宋岳，
申请(专利权)人：宁波大学，
类型：发明
国别省市：97[]