The invention provides a method for manufacturing a multi - shape alumina particle combined toughening silicon carbide ceramic, belonging to the ceramic field. The key point of the invention is that a combination of a plurality of forms of alumina particles is used as a toughening agent, the toughening material is relatively inexpensive, and the toughening material is easy to mix with other materials uniformly. The scheme of the invention takes into account both the advantages of using thermal expansion mismatch to induce micro cracks, crack deflection, crack bridging, sheet toughening, particle pulling out effect, and rod toughening particle pulling out effect, and other beneficial toughening factors.
【技术实现步骤摘要】
本专利技术涉及，属于陶瓷领域。
技术介绍
碳化硅陶瓷材料具有高温强度大、高温抗氧化性强、耐磨损性能好、热稳定性佳、热膨 胀系数小、热导率大、硬度高、抗热震和耐化学腐蚀等优良特性，在汽车、机械化工、环境保 护、空间技术、信息电子、能源等领域有着日益广泛的应用，已经成为一种在很多工业领域 性能优异的其他材料不可替代的结构陶瓷。机械设备中的动密封是通过两个密封端面材料的旋转滑动而进行的，作为密封端面材料， 要求硬度高，具有耐磨损性。碳化硅陶瓷的硬度相当高且摩擦系数小，故碳化硅陶瓷作为机 械密封端面材料可获得其它材料所无法达到的滑动特性。另一方面，两个端面密封材料在旋 转运动过程中由于摩擦会产生一定的热量，从而使密封端面的局部温度升高，因此端面材料 还必须能够耐受一定的温度。为了避免端面密封材料在旋转滑动过程中产生热应变和热裂， 要求端面材料的导热系数高、抗热震性好。目前，碳化硅陶瓷已经在各类机械密封中获得大 量的应用，并为机械设备的省力和节能做出了很大的贡献，显示出其他材料所无法比拟的优 越性。碳化硅陶瓷在机械工业中还被成功地用作各种轴承、切削刀具。航空航天、原子能...
【技术保护点】
多形态氧化铝颗粒组合增韧碳化硅陶瓷制造方法，该制造方法的主要原料是碳化硅粉、烧结助剂、增韧料以及结合剂，经混合、成型、固化、高温烧结等主要工艺步骤，形成碳化硅陶瓷产品，原料中含有的增韧料是为增加碳化硅陶瓷的韧性而加入的物料，所述高温烧结工艺步骤的烧结方式是无压固相烧结或无压液相烧结，其特征在于，所采用的增韧料是由三种不同形态的氧化铝颗粒构成，所述三种不同形态的氧化铝颗粒是球状氧化铝颗粒、棒状氧化铝颗粒以及片状氧化铝颗粒，所述增韧料是由颗粒形貌呈球状的氧化铝颗粒以及颗粒形貌呈棒状的氧化铝颗粒以及颗粒形貌呈片状的氧化铝颗粒构成的氧化铝粉，所述增韧料是多形态氧化铝颗粒组合增韧料，...
【技术特征摘要】
...
【专利技术属性】
技术研发人员：李榕生，水淼，王霞，宋岳，
申请(专利权)人：宁波大学，
类型：发明
国别省市：97[中国|宁波]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。