含有雾化炼钢炉渣的混凝土组合物以及利用该混凝土组合物的混凝土砖制造技术

本发明专利技术提供了一种含有雾化炼钢炉渣球（也称为ＰＳ球）的混凝土组合物。更具体地，本发明专利技术提供了含砂子的混凝土组合物，其中雾化炼钢炉渣球部分地或者完全地代替了所述砂子。本发明专利技术的混凝土组合物由水、水泥、粒度大于５ｍｍ的粗骨料、粒度小于５ｍｍ的细骨料、任选添加剂、以及其他不可避免的杂质的余量组成，其中所述细骨料包括大于３０ｖｏｌ．％的雾化炉渣球。

Concrete composition containing atomized steelmaking slag and concrete brick using the same

The present invention provides a concrete composition containing atomized steel slag balls (also called PS balls). More specifically, the present invention provides a sand containing concrete composition in which the molten steel slag ball is partially or completely substituted for the sand. The composition of concrete composition of the invention is composed of water, cement, coarse aggregate particle size greater than 5mm, particle size less than 5mm fine aggregate and optional additives, and the balance of other inevitable impurities, wherein the fine aggregate comprises more than 30vol.% of atomized slag ball.

【技术实现步骤摘要】
【国外来华专利技术】
本专利技术涉及一种含有雾化炼钢炉渣球(也称为PS (精制炉渣 (Precious Slag))球)的混凝土组合物。更具体地，本专利技术涉及含砂 子的混凝土组合物，其中雾化炼钢炉渣球部分地或者完全地代替了所 述砂子。
技术介绍
通常，混凝土是利用水泥和水在反应时的固化现象的水捏合的水 泥浆和建筑骨料的夯实混合物。混凝土技术规范也明确定义了混凝土 的标准要求。在回顾这个技术规范时，我们可以看出混凝土是由水泥、 水、粗骨料、细骨料、以及混凝土添加剂等组成。根据混凝土技术规范，混凝土组合物中的细骨料是指达到下列表 1中的粒度分布要求的骨料。除了表1中给出的详细的范围和要求之外， 为了保证混凝土的高性能，也必须满足以下的要求洁净，高强度和 耐受性，不含有诸如灰尘、泥土、有机杂质、盐之类的有害物质。另 外，混凝土的颗粒外形应该呈正方或者圆形，表面结构与水泥之间具 有高粘附力，足够达到要求的重量以避免因为太轻而产生的材料断裂 的危险，以及任选的耐磨性。表1:<table>table see original document page 5</column&gt;</row本文档来自技高网...

【技术保护点】
一种混凝土组合物，包括水、水泥、粒度大于５ｍｍ的粗骨料、粒度小于５ｍｍ的细骨料、任选添加剂、以及其他不可避免的杂质的余量，其中所述细骨料包括大于３０ｖｏｌ．％的雾化炉渣球。

【技术特征摘要】
【国外来华专利技术】...

【专利技术属性】
技术研发人员：吴玉洙，吴相润，
申请(专利权)人：株式会社艾克玛斯特，
类型：发明
国别省市：KR[韩国]