梯度多孔陶瓷膜及其制备方法技术

本发明专利技术涉及一种梯度多孔陶瓷膜，孔径尺寸为０．１－１００μｍ，孔隙率为２０－９０％，孔隙定向排列，孔具有定向开口连通性且孔径在厚度方向上梯度变化，制备方法是按陶瓷粉体∶去离子水∶聚丙烯酸铵∶聚乙烯醇∶聚乙二醇＝０．１～０．８∶０．２～０．８∶０．００１～０．１∶０．０５～０．５∶０．０５～０．８（重量比）进行球磨混合，得到的浆料经真空除泡后在金属衬底上进行流延成型，通过刮刀控制膜厚度。流延膜经低温冷冻，真空干燥以及脱粘烧结后，得到孔隙率高且可控的梯度多孔陶瓷膜，有望在催化剂载体、分级吸附催化膜、过滤器件等领域具有好的应用前景。

Gradient porous ceramic film and preparation method thereof

The present invention relates to a gradient porous ceramic membrane, pore size of 0.1 to 100 mu m, the porosity is 20 - 90%, pore orientation, directional opening connectivity and pore gradient in the thickness direction changes with holes, the preparation method is according to the ceramic powder: Deionized water, ammonium polyacrylate, polyvinyl alcohol, polyethylene glycol = 0.1 to 0.8: 0.2 to 0.8: 0.001 to 0.1: 0.05 to 0.5: 0.05 ~ 0.8 (weight ratio) was mixed by milling the slurry by vacuum casting in removing the metal substrate by bubbles, scraper film thickness control. Casting film by low temperature freezing, vacuum drying and debonding after sintering, porous gradient ceramic membrane with high porosity and controllable, is expected to has a good application prospect in catalyst carrier, grade adsorption catalytic membranes, filter etc..

【技术实现步骤摘要】

本专利技术涉及一种，更确切的说是利 用流延法结合冷冻千燥工艺制备出具有开口定向孔结构和高孔隙率 以及孔径在膜厚度方向梯度变化的多孔陶瓷膜的制备方法，属于多孔 陶瓷领域。
技术介绍
多孔陶瓷材料由于耐化学腐蚀、耐磨、耐高温，以及轻质、高渗 透率、具有大的比表面积等优点，在常温及高温过滤器件、催化剂载 体以及无机反应分离器件等领域具有广阔的应用前景。关于多孔陶瓷 的制备方法有很多报道，例如，方旭东等人(中国专利，专利号200410041065)采用a-Al203为主要原料，以氧化钙和稀土氧化物为 添加剂，通过高温下的烧结反应形成结构性开口微孔、微孔大小均匀 且机械强度高的氧化铝多孔陶瓷，在用作催化剂载体时能够担载更多 的催化剂，且催化反应率高；CN200410067101采用泡沫浸渍法制备 出了大孔径、网眼结构孔隙的碳化硅多孔陶瓷，通过采用 MgO-Al2(VSi02体系作为烧结体系，在120(TC 140(TC的温度下实 现对网眼多孔碳化硅陶瓷的烧结，制备了抗压强度在l.OMPa以上、且孔径在500pm 4mm范围内调控、耐火度在1580。C 1730。C的网眼 碳化硅多孔陶瓷，可以本文档来自技高网...

【技术保护点】
梯度多孔陶瓷膜，其特征在于孔径尺寸为０．１－１００μｍ，孔隙率为２０－９０％，孔隙定向排列，孔具有定向开口连通性且孔径在厚度方向上梯度变化。

【技术特征摘要】

【专利技术属性】
技术研发人员：曾宇平，任琳琳，江东亮，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明
国别省市：31[中国|上海]