The invention discloses a metal door produced by expansion perlite with lightweight fireproof filling material and preparation method thereof, which includes swelling perlite, Magnesium Oxide, Magnesium Sulfate, slaked lime, water soluble adhesive, waterproof agent, bulk density between 200 ~ 300kg / M = 3, ratio of the components by weight percentage respectively: swelling perlite is 45 ~ 65, 15 ~ 25 Magnesium Oxide, Magnesium Sulfate 5 ~ 15, 0.5 ~ 4 hydrated lime, water soluble adhesive is 2 ~ 5; after the adoption of the technical scheme, the production of products with high mechanical strength, light weight, high fire resistance rating, sound absorption, strong weatherability, good effect thermal insulation and energy saving, the production is simple, non-toxic no radiation etc.; the products can be widely used in metal door industry, building materials industry and related industries.
【技术实现步骤摘要】
本专利技术涉及 一 种轻质材料，特别是 一 种可用于防盗门、防 火门、钢质进户门等金属门的门内填充料、建筑材料等行业的 轻质防火填充料及制备方法。
技术介绍
目前，生产的防盗门、防火门、钢质进户门等金属门 一 般 选用蜂窝纸和硅酸钙板夹硅酸铝棉为填充料。蜂窝纸存在的不足之处是遇火会燃烧，没有防火性能，吸声隔音及隔热保温 性能差，易受潮，遇水会软化，防水耐水性能差。硅酸锦板夹 硅酸铝棉存在的不足之处是耐火等级低，遇高温会产生熔化， 起不到防火作用，生产成本高，石棉刺手，粉尘吸入对人体损 害大，为此国家环保总局在2 0 0 5年就明确规定，家用制品中不 得含有石棉，粘合剂不得含有甲醛、苯等有害物质。防盗门、 防火门、钢质进户门等金属门迫切需要一种防火等级高、机械 强度好、生产安装方便、成本低的新型门内填充料。而目前使用的建筑材料 一 般以粘土砖、水泥制品为主，其 缺点是重量重、强度低、隔音隔热防火效果差；虽然有关科研 机构、生产厂家及有识之士针对存在的上述问题进行了开发和 研究，如国家知识产权局在2 0 0 5年8月24日授权公告的 一 种轻质隔音隔热防火建筑材料及...
【技术保护点】
一种利用膨涨珍珠岩生产金属门用轻质防火填充料，其特征是：它包含膨涨珍珠岩、氧化镁、硫酸镁、熟石灰、水溶性粘接剂、防水剂，容重在２００～３００ｋｇ／ｍ↑［３］之间，各成份按重量百分比的配比分别为：膨涨珍珠岩４５～６５；氧化镁１５～２５；硫酸镁５～１５；熟石灰０．５～４；水溶性粘接剂２～５；防水剂１～６。
【技术特征摘要】
【专利技术属性】
技术研发人员：应连希，
申请(专利权)人：永康市美信实业有限公司，
类型：发明
国别省市：33[中国|浙江]