本发明专利技术涉及一种钢筋混凝土表面防腐剂，它含有活性聚氧硅烷２．２～３．２份，异丁基三乙氧基硅烷１．６～２．４份，六甲基硅烷０．６～１．３份，活性扩散剂０．７～１．２份，油性溶剂２．５～３．５份，以该钢筋混凝土表面防腐剂总重量为基准。本发明专利技术的钢筋混凝土防腐剂对混凝土性质无任何负面影响，成本低廉，且具有高效、长久的防腐性能，可广泛适用于沿海及内陆地区建筑，如海港码头、跨海大桥、水库、电厂水塔，高架桥，地下管道，人防工程、石材表面、污水处理池等大气恶劣区混凝土建筑物的防腐工作。

Surface preservative for reinforced concrete

The invention relates to a reinforced concrete surface preservative, it contains active polysiloxane from 2.2 to 3.2, isobutyl triethoxysilane from 1.6 to 2.4, six from 0.6 to 1.3 methyl silane, active diffusion agent 0.7 ~ 1.2, 2.5 ~ 3.5 servings of oily solvent, on the surface of the reinforced concrete preservatives total weight as a benchmark. Reinforced concrete preservatives of the invention without any negative effect on concrete properties, low cost, and has high efficiency, long anticorrosion performance, can be widely used in coastal and inland areas such as building, bridge, wharf, power plant, reservoir water tower, under the viaduct, pipeline, anticorrosion work of civil air defense projects, stone concrete buildings the surface, sewage treatment pond area bad atmosphere.

【技术实现步骤摘要】

本专利技术涉及一种建筑材料，特别涉及一种钢筋混凝土表面防腐剂。技术背景目前随着现代混疑土技术与我国经济的快速持续n混凝土^皮广泛应用 于港口、大坝、公路、桥梁、市政等现代化工程建设中，然而，钢筋混凝土结 构由于受到各种环境条件，如大气、水等物理或化学的侵蚀作用，即使结构设 计合理、施工正确，在其使用期间也往往会发生劣化，使其未达到预期寿命而 被破坏，而由于钢筋混凝土结构的破坏和腐蚀，给各类建筑和工程造成了重大 的安全隐患和经济损失。据报道，在美国，需要大量的资金来修复净M蚀破坏的钢筋混凝土结构；在英国，需要重修或大修的钢筋混凝土结构占36%;在中 国，钢筋混凝土结构的侵蚀破坏也十分严重，有的海港码头^A使用三年左右， 码头梁板就出现锈斑、细微裂缝等轻微的破坏，绝大多数海工结构因未采:^it 当的防腐蚀措^不到十年内均出现严重的侵蚀破坏,造成了极大的经济损失， 例如连云港，宁波北仑港的码头使用8年左右，承重梁内部钢筋便出现大面 积的锈蚀；舟山某军港码头纵横箍筋出现锈断，因未进行有效的防腐蚀处理而 才l菱。而在我国的北方城市，如北京和天津的立交桥因冬季喷洒除水盐而造成 桥梁构件出现本文档来自技高网...

【技术保护点】
一种钢筋混凝土表面防腐剂，其特征在于，其组成及配比为：活性聚氧硅烷：２．２～３．２份异丁基三乙氧基硅烷：１．６～２．４份六甲基硅烷：０．６～１．３份活性扩散剂：０．７～１．２份油性溶剂：２．５～３．５ 份以上份数均为质量份数。

【技术特征摘要】

【专利技术属性】
技术研发人员：秦为民，
申请(专利权)人：常州源康化工有限公司，
类型：发明
国别省市：32[中国|江苏]