The present invention relates to the field of unshaped castable, especially refractory castable for coal-fired heating furnace, coal-fired heating furnace has a furnace wall, the upper end of the two side of the furnace wall with unshaped refractory material pouring arch furnace integrated structure of furnace wall and arch, arch arch of the connection between the transition zone and the at the angle of poured fill unshaped refractory castable, weight percentage of unshaped refractory castable is high alumina cement is 15% ~ 20%, 15% fine powder and fine aggregate (1 ~ 3) ranged from 15% to 20%, in the aggregate (5 ~ 10) was 10%, the coarse aggregate is 35%, the balance water, strengthen the firmness of the whole structure.
【技术实现步骤摘要】
本专利技术涉及不定型浇注料领域,尤其是一种用于燃煤加热炉的不定型耐火浇注料。
技术介绍
近年来,随着人类社会对能源消耗的日益增加,国际、国内市场油、气价格的不断上涨,造成燃油、燃气锅炉运行成本的大幅度提高。迫使燃油、燃气锅炉使用的单位要寻找运行成本较低,并能满足使用要求的新一代锅炉产品来代替现有的燃油、燃气锅炉,目前,现有的燃煤加热炉的炉拱多是用砖砌成的,容易损坏,影响加热的效果。
技术实现思路
本专利技术要解决的技术问题是提供一种用于燃煤加热炉的不定型耐火浇注料。 本专利技术解决其技术问题所采用的技术方案是一种用于燃煤加热炉的不定型耐火浇注料,燃煤加热炉具有炉墙,炉墙的两侧面上端用不定型耐火浇注料浇注了一体结构的拱形炉拱,炉墙和拱形炉拱间的连接过渡区和斜角处浇填不定型耐火浇注料,不定型耐火浇注料的重量百分比含量是高铝水泥为15%~20%、细粉为15%、细骨料(1~3目)为15%~20%、中骨料(5~10目)为10%、粗骨料为35%,余量为水。 本专利技术的有益效果是,本专利技术的用于燃煤加热炉的不定型耐火浇注料,使炉拱结构坚固,使用寿命长,且还可以用在其它结构上。 附图说明 下面结合附图和实施例对本专利技术进一步说明。 图1是本专利技术用于燃煤加热炉的不定型耐火浇注料的主视图的剖视图; 图2是本专利技术用于燃煤加热炉的不定型耐火浇注料的左视图的剖视图。 图中1.拱形结构,2.炉墙。 具体实施例方式 如图1、图2所示的最佳实时方式的用于燃煤加热炉的不定型耐火浇注料,燃煤加热炉具有炉墙2,炉墙2的两侧面上端用不定型耐火浇注料浇注了一体 ...
【技术保护点】
一种用于用于燃煤加热炉的不定型耐火浇注料,其特征是:燃煤加热炉具有炉墙(2),炉墙(2)的两侧面上端用不定型耐火浇注料浇注了一体结构的拱形炉拱(1),不定型耐火浇注料的重量百分比含量是高铝水泥为15%~20%、细粉为15%、细骨料(1~3目)为15%~20%、中骨料(5~10目)为10%、粗骨料为35%,余量为水。
【技术特征摘要】