The present invention provides a method for producing low viscosity epoxy resin, which comprises the following steps: distillation of epoxy resin raw materials, have low epoxy equivalent epoxy resin; the low epoxy resin and epoxy equivalent to reduce the viscosity of mixed epoxy resin, low viscosity epoxy resin. The production process of epoxy resin without the need to change the existing method provided by the invention, only need to separate the epoxy resin products available, and the obtained low epoxy equivalent epoxy resin and epoxy resin were mixed to reduce the viscosity of epoxy resin with low viscosity can be obtained. Moreover, the method provided by the invention can realize the control of the total chlorine in the epoxy resin. The results show that the viscosity of the low viscosity epoxy resin is 7000 ~ 10000mPa.s, and the total chlorine is from to 1600ppm.
【技术实现步骤摘要】
本专利技术涉及环氧树脂
，特别涉及一种低粘度环氧树脂的生产方法。
技术介绍
环氧树脂是一种分子结构含有二个或二个以上环氧基的高分子化合物。环氧树脂因其具有良好的加工性、稳定性、低吸水性、电绝缘性和较高的机械强度，以及加固化剂后有高度的粘合性等优点，被广泛用于涂料行业、机械行业、电子行业、交通运输业、汽车制造业、建筑业和航空航天等领域。随着我国国民经济快速、稳健发展，环氧树脂行业也得到了长足进步。近几年，中国环氧树脂的需求量以每年15％的速度递增，尤其是电子、涂料等行业用的高品质环氧树脂更以每年20％～25％的速度递增，具有很大的市场前景。目前，市场较多的产品为环氧当量为184～194g/eq的标准环氧树脂。然而，由于标准环氧树脂具有很高的粘度，该高粘度特性决定了其不能够满足某些只需较低粘度的领域需求。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种环氧树脂的生产方法。本专利技术制备得到的环氧树脂具有良好的低粘度特性。为了实现上述...
【技术保护点】
一种低粘度环氧树脂的生产方法，包括以下步骤：对环氧树脂原料进行蒸馏分离，得到低环氧当量环氧树脂；将所述低环氧当量环氧树脂与待降低粘度环氧树脂混合，得到低粘度环氧树脂。
【技术特征摘要】
1.一种低粘度环氧树脂的生产方法，包括以下步骤：
对环氧树脂原料进行蒸馏分离，得到低环氧当量环氧树脂；
将所述低环氧当量环氧树脂与待降低粘度环氧树脂混合，得到低粘度环氧
树脂。
2.根据权利要求1所述的生产方法，其特征在于，所述低环氧当量环氧树
脂的环氧当量为170～176g/eq，所述低环氧当量环氧树脂的总氯为
400～1200ppm。
3.根据权利要求1所述的生产方法，其特征在于，所述待降低粘度环氧树
脂的环氧当量为180～194g/eq。
4.根据权利要求1或3所述的生产方法，其特征在于，所述低环氧当量环
氧树脂与待降低粘度环氧树脂的质量比为(0.1～3)∶1。
5.根据权利要求1所述的生产方法，其特征在于，所述环氧树脂原料的环
氧当量为180～194g/eq。<...
【专利技术属性】
技术研发人员：俞孝伟，杨颖，孙祥，宋数宾，马良，宋桂成，
申请(专利权)人：江苏扬农锦湖化工有限公司，江苏扬农化工集团有限公司，
类型：发明
国别省市：江苏;32