The invention relates to a starch based water absorbing resin and a preparation method thereof, which belongs to the technical field of water absorbing resin. The present invention includes 40 potato starch 50, 30 40 methacrylic acid and acrylic acid, acrylonitrile 5 30 40 10, 1 2 methylene bis acrylamide, ethylene glycol dimethacrylate 0.5 1, 1 3 potassium persulfate and sodium bicarbonate 1 3, distilled water 80 100 copies, 30 copies of 10%NaOH20. This kind of water absorbent resin is a kind of raw material, which has the advantages of environmental friendly, biodegradable, low emission, low cost, easy to obtain raw materials and so on. Water absorption rate of up to 600 800g/g.
【技术实现步骤摘要】
本专利技术涉及一种吸水树脂及其制备方法,更具体地说,本专利技术涉及一种淀粉基吸水树脂及其制备方法,属于吸水树脂
技术介绍
高吸水性树脂是一种新型功能高分子材料,它能吸收自身质量几百倍甚至上千倍的水,吸水后的材料以凝胶的形式存在,在外力或者加压的情况下水分也不会流失,所以具有良好的保水能力,故高吸水性材料在工业、农业、医疗卫生等各个行业都有着重要的作用。淀粉接枝系高吸水性树脂是一种含有亲水基团的新型高分子网状聚合物材料,具有极强的吸水性能,其产品具有广泛的用途,现己渗透到农业、石油工业、医药卫生等各个领域。
技术实现思路
本专利技术旨在解决现有技术中的吸水树脂的问题,提供一种淀粉基吸水树脂,该吸水树脂环境友好、可生物降解、减排、成本低、原料易于获取、吸水倍率高。为了实现上述专利技术目的,其具体的技术方案如下:一种淀粉基吸水树脂,其特征在于:包括以下按照重量份数计的原料:马铃薯淀粉40-50份甲基丙烯酸30-40份丙烯酸30-40丙烯腈5-10份亚甲基双丙烯酰胺1-2份双甲基丙烯酸乙二醇酯0.5-1.0份过硫酸钾1-3份碳酸氢钠1-3份蒸馏水80-100份10%NaOH20-30份。一种淀粉基吸水树脂的制备方法,其特征在于:包括以下工艺步骤:A、在一容器中加入淀粉,用蒸馏水搅拌混合,直至淀粉完全分散于蒸馏水中;将体系环境温度升至60-65℃,保温2-3h,使淀粉发生糊化;将糊化淀粉温度冷却至室温,备用;B、将淀粉糊冷却以后加入氧化-还原引发剂,搅拌混合均匀;加入预先经10%NaOH中和过的甲基丙烯酸和丙烯酸和丙烯腈以及交联剂亚甲基双丙烯酰胺和双甲基丙烯 ...
【技术保护点】
一种淀粉基吸水树脂,其特征在于:包括以下按照重量份数计的原料:马铃薯淀粉 40‑50份甲基丙烯酸 30‑40份丙烯酸 30‑40丙烯腈 5‑10份亚甲基双丙烯酰胺 1‑2份双甲基丙烯酸乙二醇酯 0.5‑1.0份过硫酸钾 1‑3份碳酸氢钠 1‑3份蒸馏水 80‑100份10%NaOH 20‑30份。
【技术特征摘要】
1.一种淀粉基吸水树脂,其特征在于:包括以下按照重量份数计的原料:马铃薯淀粉40-50份甲基丙烯酸30-40份丙烯酸30-40丙烯腈5-10份亚甲基双丙烯酰胺1-2份双甲基丙烯酸乙二醇酯0.5-1.0份过硫酸钾1-3份碳酸氢钠1-3份蒸馏水80-100份10%NaOH20-30份。2.根据权利要求1所述的一种淀粉基吸水树脂的制备方法,其特征在于:包括以下工艺步骤:A、在一容器中加入淀粉,用蒸馏水搅拌混合,直至淀粉完全分散于蒸馏水中;将体系环境温度升至60-6...