The invention discloses a waterproof solid wood floor, which belongs to the technical field of building material preparation. The finishing process it is first in the wood floor surface coated with a layer of paint, and in which the surface of the wood floor is coated with a layer of waterproof coating, waterproof coating made of the following raw materials in parts by weight: chlorinated rubber resin 80 ~ 100, 5 ~ 8 nanometer silicon carbide and turpentine 5 ~ 8, 5 ~ 10 pigment, Pinonic acid 10 ~ 15, two peroxide cumene 2 to 6 copies, 2 copies to 6 copies of terpineol, sodium carboxymethyl cellulose 2 ~ 6 and propylene glycol butyl ether 1 ~ 4. The present invention a-terpineol prepared special waterproof coating by adding certain proportion in the coating on the substrate of nano silicon carbide, turpentine, paint, Pinonic acid and peroxide cumene, two, and the surface of the waterproof coating of solid wood flooring, solid wood flooring which has excellent waterproof performance.
【技术实现步骤摘要】
本专利技术属于建筑材料
，尤其涉及一种防水实木地板。
技术介绍
为了防止实木地板因吸水而出现长霉、开裂、变形等形象，一般会对实木地板进行防水处理。然而，现有的防水处理方法得到的实木地板，其防水效果依然不太理想。
技术实现思路
本专利技术是提供一种防水实木地板，解决了现有的防水处理方法得到的实木地板，其防水效果依然不太理想的问题。为了解决上述技术问题，本专利技术所采用的技术方案是：它的涂饰工艺是先在木地板的表面涂覆一层普通油漆，再在木地板的表面涂覆一层防水涂层，其中，所述防水涂层采用以下重量份数的原料制成：氯化橡胶树脂80份～100份、纳米碳化硅5份～8份、松节油5份～8份、颜料5份～10份、蒎酮酸10份～15份、过氧化二异丙苯2份～6份、松油醇2份～6份、羧甲基纤维素钠2份～6份以及丙二醇丁醚1份～4份。由于采用上述技术方案，本专利技术具有如下有益效果：本专利技术通过在涂料基材上添加特定比例的纳米碳化硅、松节油、颜料、蒎酮酸、过氧化二异丙苯、松油醇制得特殊的防水涂料，并将该防水涂料涂覆实木地板的表面，从而使实木地板具有较好的防水性能。具体实施方式以下结合具体实...
【技术保护点】
一种防水实木地板，它的涂饰工艺是先在木地板的表面涂覆一层普通油漆，再在木地板的表面涂覆一层防水涂层，其特征在于：所述防水涂层采用以下重量份数的原料制成：氯化橡胶树脂80份～100份、纳米碳化硅5份～8份、松节油5份～8份、颜料5份～10份、蒎酮酸10份～15份、过氧化二异丙苯2份～6份、松油醇2份～6份、羧甲基纤维素钠2份～6份以及丙二醇丁醚1份～4份。
【技术特征摘要】
1.一种防水实木地板，它的涂饰工艺是先在木地板的表面涂覆一层普通油漆，再在木地板的表面涂覆一层防水涂层，其特征在于：所述防水涂层采用以下重量份数的原料制成：氯化橡胶树脂80份～10...
【专利技术属性】
技术研发人员：王嘉龙，
申请(专利权)人：柳州市亿廷贸易有限责任公司，
类型：发明
国别省市：广西;45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。