The invention belongs to the technical field of manganese-zinc ferrite core, and discloses an improved structure for sintering adhesion of large products, including multiple overlapping sintering frame moulds. The features of the invention are that the sintering frame moulds are rectangular, and a middle column is arranged in the middle of the sintering frame moulds, and the height of the middle column is lower than around the moulds. The middle column is made of rigid material and the number is one. It can effectively improve the sintering adhesion of high permeability products such as large ET type, and improve the appearance quality and qualified rate.
【技术实现步骤摘要】
一种大产品烧结粘连的改进结构
本专利技术属于锰锌铁氧体磁芯
，具体地涉及一种大产品烧结粘连的改进结构。
技术介绍
高磁导率锰锌铁氧体材料主要用于各类电子产品，综合业务数字网(ISDN)、局域网(LAN)、宽域网(WAN)、背景照明等领域的脉冲变压器，抗电磁波滤波器等领域。这些领域的磁芯基本上是在弱场下工作，材料的高磁导率就会显示出独特的优越性。如图1，高磁导率锰锌铁氧体烧结的时候因为产品性能的缘故，需要叠放烧结，且中间不能晒氧化锆粉，这样烧结出来的产品才能电感高一致性好。但是因为大产品堆叠高度越高，受压面积大，导致烧结之后坯件之间接触发生反应，最后粘连在一起，导致产品分离的时候，存在损坏的问题，导致外观不良(图2)。
技术实现思路
本专利技术旨在克服现有技术的缺陷，针对上述问题，提供了一种大产品烧结粘连的改进结构，该产品用于解决高磁导率锰锌铁氧体在烧结工序叠烧粘连的问题，可用于ET型、切割型EE型等高磁导率产品。结合实际的工作经验，精心设计，能够有效改善大ET型等高磁导率产品烧结粘连的问题，提高外观质量及合格率。为了解决上述技术问题，本专利技术提供以下技术方案：一种大产品烧结粘连的改进结构，包括多个叠放的烧结框模具1，其特征在于，烧结框模具1为矩形，烧结框模具中部设置有中柱11，中柱高度低于模具四周。优选的，中柱为刚性材料制成，数量为一根。与现有技术相比较，本专利技术具有如下的有益效果：中柱位置比四周下沉0.1mm，这样在大产品叠烧的时候，中柱位置不相互接触，就能有效减少中间位置粘连的问题。此设计方案只适用于结构较大的产品上，如ET28以上，因为其中柱自...
【技术保护点】
1.一种大产品烧结粘连的改进结构，包括多个叠放的烧结框模具(1)，其特征在于，烧结框模具(1)为矩形，烧结框模具中部设置有中柱(11)，中柱高度低于模具四周。
【技术特征摘要】
1.一种大产品烧结粘连的改进结构，包括多个叠放的烧结框模具(1)，其特征在于，烧结框模具(1)为矩形，烧结框模具中部设置有中柱...