The present invention relates to a preparation method of pressure-sensitive adhesives, which mixes the raw materials of pressure-sensitive adhesives and plasticizes them, and then adds the obtained mixture into organic solvents, which can be obtained after mixing evenly. The raw materials of pressure-sensitive adhesives include 30-50 parts of natural rubber, 15-20 parts of styrene-butadiene rubber, 8-12 parts of acrylic resin, 30-40 parts of terpene resin and 8-20 parts of phenolic resin. 12 copies. The pressure sensitive adhesive of the invention has low cost, strong bonding force, no glue overflow phenomenon in the use process, and simple process.
【技术实现步骤摘要】
一种压敏胶黏剂的制备方法
本专利技术涉及一种压敏胶黏剂的制备方法。
技术介绍
压敏胶黏剂是一类具有对压力有敏感性的胶粘剂。主要用于制备压敏胶带。一般压敏胶的剥离力（胶粘带与被粘表面加压粘贴后所表现的剥离力）<胶粘剂的内聚力（压敏胶分子之间的作用力）<胶粘剂的粘基力（胶粘剂与基材之间的附着力）。压敏胶黏剂按照主体树脂成分可成分可分为橡胶型和树脂型两类。现有技术的压敏胶黏剂成本较高，粘结力不高，在使用过程中易产生溢胶现象。
技术实现思路
本专利技术的目的在于提供一种解决上述问题的压敏胶黏剂的制备方法。技术方案一种压敏胶黏剂的制备方法：将压敏胶黏剂原料混合后塑炼，然后将得到的混合物加入到有机溶剂中，混合均匀后即得；所述压敏胶黏剂原料包括如下重量份的组分：天然橡胶30～50份，丁苯橡胶15～20份，丙烯酸树脂8～12份，萜烯树脂30～40份，酚醛树脂8～12份。进一步，所述有机溶剂为二甲苯。进一步，塑炼后得到的混合物与有机溶剂的重量比为1:2-5。本专利技术的压敏胶黏剂成本低，粘结力强，在使用过程中不会出现溢胶现象，并且工艺简单。具体实施方式下面结合具体实施例对本专利技术作进一步说明。实施例1一种压敏胶黏剂的制备方法：将压敏胶黏剂原料混合后塑炼，然后将得到的混合物加入到有机溶剂二甲苯中，混合物与有机溶剂的重量比为1:5，混合均匀后即得；所述压敏胶黏剂原料包括如下重量份的组分：天然橡胶50份，丁苯橡胶15份，丙烯酸树脂12份，萜烯树脂30份，酚醛树脂8份。实施例2一种压敏胶黏剂的制备方法：将压敏胶黏剂原料混合后塑炼，然后将得到的混合物加入到有...
【技术保护点】
1.一种压敏胶黏剂的制备方法，其特征在于，将压敏胶黏剂原料混合后塑炼，然后将得到的混合物加入到有机溶剂中，混合均匀后即得；所述压敏胶黏剂原料包括如下重量份的组分：天然橡胶30～50份，丁苯橡胶15～20份，丙烯酸树脂8～12份，萜烯树脂30～40份，酚醛树脂8～12份。
【技术特征摘要】
1.一种压敏胶黏剂的制备方法，其特征在于，将压敏胶黏剂原料混合后塑炼，然后将得到的混合物加入到有机溶剂中，混合均匀后即得；所述压敏胶黏剂原料包括如下重量份的组分：天然橡胶30～50份，丁苯橡胶15～20份，丙烯酸树脂8～12份，...