The invention discloses a method for communication pipeline of multi walled PVC formula, which is characterized in that the weight made of the following raw materials: PVC resin 60 100 copies, 7 copies of 4 calcium stearate, sebacic acid octyl two 2 7 1 3, styrene butadiene rubber, lubricants 2 8 copies, 0.5 PE wax 3, six methyl three phosphoryl amine 6 8 copies, 2 copies of 1 rare earth stabilizer, polyethylene wax 2 3 copies, 1.3 copies of 0.5 additives. The beneficial effect of the invention is: using PVC resin as the main raw material with high temperature and high pressure extrusion molding, cold resistant, impact resistance, high temperature resistance, and long service life, for the laying of underground communication pipeline, to protect the cable, communication cable, and a relatively low, suitable for popularization and application.
【技术实现步骤摘要】
一种用于通信管道的多壁PVC配方
本专利技术涉及塑胶管道
,具体涉及一种用于通信管道的多壁PVC配方。
技术介绍
PVC管材的主要成分是聚氯乙烯,另外加入其它成分来增强其耐热性、韧性、延展性等。PVC在当今世界上深受喜爱,是颇为流行并广泛应用的一种合成材料。PVC管材是一种成熟的管材,主要应用于给排水工程。PVC管材具有耐酸、耐碱、耐腐蚀、强度高等优点,但抗冲性能比较差。
技术实现思路
本专利技术提供一种用于通信管道的多壁PVC配方,利用该配方制造出来的PVC管材可以增强抗冲性能及强度。为达到上述目的,本专利技术一种用于通信管道的多壁PVC配方,其特征在于由下列重量份的原料制成:PVC树脂60-100份,硬脂酸钙4-7份,葵二酸二辛酯2-7份,丁苯橡胶1-3份,润滑剂2-8份,PE蜡0.5-3份,六甲基磷酰三胺6-8份,稀土稳定剂1-2份,聚乙烯蜡2-3份,助剂0.5-1.3份。作为优选,由下列最优配比原料制成:PVC树脂80份,硬脂酸钙3.7份,葵二酸二辛酯4份,丁苯橡胶2份,润滑剂4份,PE蜡2份,六甲基磷酰三胺7份,稀土稳定剂1.4份,聚乙烯蜡2.6份,助剂0.6份。作为优选,助剂为增塑剂、润湿剂、稳定剂中的一种或两种以上组成。本专利技术的有益效果是:采用PVC树脂为主要原料,经高温高压挤压成型,抗冲击,耐高温,耐寒,使用寿命长,用于地下通信管道的铺设,对通信光缆、电缆起到保护作用,而且成比较低,适合推广应用。具体实施方式以下对本专利技术的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本专利技术,并不用于限定本专利技术。实施例 ...
【技术保护点】
一种用于通信管道的多壁PVC配方,其特征在于由下列重量份的原料制成:PVC 树脂 60‑100 份,硬脂酸钙 4‑7 份,葵二酸二辛酯 2‑7 份,丁苯橡胶1‑3份,润滑剂2‑8份,PE蜡0.5‑3份,六甲基磷酰三胺 6‑8 份,稀土稳定剂 1‑2 份,聚乙烯蜡 2‑3 份,助剂0.5‑1.3 份。
【技术特征摘要】
1.一种用于通信管道的多壁PVC配方,其特征在于由下列重量份的原料制成:PVC树脂60-100份,硬脂酸钙4-7份,葵二酸二辛酯2-7份,丁苯橡胶1-3份,润滑剂2-8份,PE蜡0.5-3份,六甲基磷酰三胺6-8份,稀土稳定剂1-2份,聚乙烯蜡2-3份,助剂0.5-1.3份。2.如权利要求1所述的一种用于通信管道的多壁PV...