本发明专利技术提出了凸轮轴浇注系统，包括浇口杯、内浇口、凸轮轴型腔，浇口杯与内浇口直接连接，内浇口与凸轮轴型腔的接口处放置有纤维滤网。进一步改进，浇口杯处设有泡沫陶瓷滤网。本发明专利技术在内浇道与凸轮轴型腔的结合处设置纤维滤网，浇注完毕后，相当于铁液凝固后在内浇道和铸件之间形夹杂物从而在该位置断裂，用很小的力就能剥离浇口，这样可以有效避免去除浇注系统时对凸轮轴本身的损伤，完全避免了凸轮轴折断。泡沫陶瓷与纤维滤网形成两级过滤，保证铁水的纯净度。

Camshaft gating system

The invention relates to a camshaft pouring system, which comprises a gate cup, an inner gate and a cam shaft cavity, wherein the gate cup is directly connected with the inner gate, and a fiber filter screen is arranged at the interface between the inner gate and the camshaft cavity. Further improved, the gate cup is equipped with foam ceramic filter screen. The invention of ingate and camshaft cavity combined with fiber filter set, after the pouring, between the equivalent liquid iron after solidification of ingate and casting shaped inclusions in the position to break, with a small force to be stripped of gate, this can effectively avoid the damage of the camshaft itself the removal of gating system when, completely avoid the cam shaft breakage. Foam ceramic and fiber screen form two stage filtration to ensure the purity of molten iron.

【技术实现步骤摘要】
凸轮轴浇注系统
本专利技术涉及汽车发动机的凸轮轴制造
，尤其是凸轮轴浇注系统。
技术介绍
汽车发动机的凸轮轴是铸铁件，目前，采用的浇注系统是：浇口杯与内浇口直接连接，内浇道与凸轮轴型腔直接连接。浇注完毕后，需要人工用切割机去浇口，凸轮轴刚度较低，造成去浇口的过程中凸轮轴折断。
技术实现思路
本专利技术提出凸轮轴浇注系统，保证凸轮轴铸件上的浇口容易剥离，避免凸轮轴折断。为此，本专利技术的技术方案为：凸轮轴浇注系统，包括浇口杯、内浇口、凸轮轴型腔，浇口杯与内浇口直接连接，其特征在于：内浇口与凸轮轴型腔的接口处放置有纤维滤网。对上述技术方案的进一步限定：浇口杯处设有泡沫陶瓷滤网，泡沫陶瓷与纤维滤网形成两级过滤，保证铁水的纯净度，纤维滤网除过滤外兼有剥离内浇口的作用。有益效果：本专利技术在内浇道与凸轮轴型腔的结合处设置纤维滤网，浇注完毕后，相当于铁液凝固后在内浇道和铸件之间形夹杂物从而在该位置断裂，用很小的力就能剥离浇口，这样可以有效避免去除浇注系统时对凸轮轴本身的损伤，完全避免了凸轮轴折断。附图说明图1是本专利技术的主视图。图2是本专利技术的俯视图。具体实施方式结合图1、图2所示，进一步描述本专利技术如下：凸轮轴浇注系统，包括浇口杯4、内浇口3、凸轮轴型腔1，浇口杯4与内浇口3直接连接，内浇口3与凸轮轴型腔1的接口处放置有纤维滤网2。进一步的，浇口杯4处设有泡沫陶瓷滤网5，泡沫陶瓷5与纤维滤网2形成两级过滤，可以降低浇注铁水的冲击力，保证铁水的纯净度，纤维滤网2除过滤外兼有剥离内浇口的作用。

【技术保护点】
凸轮轴浇注系统，包括浇口杯、内浇口、凸轮轴型腔，浇口杯与内浇口直接连接，其特征在于：内浇口与凸轮轴型腔的接口处放置有纤维滤网。

【技术特征摘要】
1.凸轮轴浇注系统，包括浇口杯、内浇口、凸轮轴型腔，浇口杯与内浇口直接连接，其特征在于：内浇口与凸轮轴型...