The invention discloses a textile printing coating adhesive, which comprises the following raw materials quality copies of the composition: 20 ~ 40 methyl methacrylate and butyl acrylate 50 ~ 60, 1 ~ 3 ammonium persulfate, glycidyl methacrylate 1 - 5, twelve - 6, 1 sodium octylphenol polyoxyethylene 1 - 7, 1 - 8, acrylonitrile chitin 1 - 5, 2 - 5, polysiloxane jiaquanbuzhuoji 0.1 - 3, 2, 4 two hydroxy two benzophenone from 2 to 5. The invention of printing coating binder ultraviolet resistance, heat resistance and aging resistance, yellowing, coating printing adhesive emulsion has good stability, film speed, printing coating binder printed on textiles after the formation of transparent colorless film, strong adhesion, elasticity and toughness, corrosion resistance, anti bending fold, not stiff no, not sticky, absorption of colored material.
【技术实现步骤摘要】
一种纺织印花涂料粘合剂
本专利技术涉及粘合剂
,具体涉及一种纺织印花涂料粘合剂。
技术介绍
印花涂料是指使用高分子粘合剂在织物上形成薄膜,把颜料固着在织物上的印花方法,在涂料印花中粘合剂粘合剂起着关键的作用,印花产品的手感、新鲜度、各项牢度,如水洗、干洗、摩擦度等指标,在很大程度上取决于粘合剂的质量。目前。涂料印花还存在残留甲醛、手感和牢固性差、印花浆堵网等问题。印花涂料工艺简单、色谱齐全、拼色容易固色后一般不需水洗、可节能、节水等有优点而被广泛应用,因而解决印花涂料的粘合剂的问题研发出无环境污染、无毒害、较好憎水性、良好透气性以及优良柔软性和牢固性强的印花涂料粘合剂有助于印花涂料的进一步推广和应用。
技术实现思路
本专利技术的目的在于,针对现有技术的不足,提供了一种纺织印花涂料粘合剂。为实现上述目的,本专利技术采取以下技术方案:一种纺织印花涂料粘合剂,其由质量份的以下原料组成:甲基丙烯酸甲酯20~40份、丙烯酸丁酯50~60份、过硫酸铵1~3份、甲基丙烯酸缩水甘油酯1~5份、十二烷基苯磺酸钠1~6份、辛基酚聚氧乙烯1~7份、丙烯腈1~8份、甲壳素1~5份、聚硅氧烷2~5份、甲醛捕捉剂0.1~3份、2,4-二羟基二苯甲酮2~5份。本专利技术中,甲基丙烯酸甲酯、丙烯腈为硬单体,可以高涂料的结构强度、耐磨性和耐洗涤性,粘合剂固化后粘合强度高,丙烯酸乙酯为软单体,提高粘合剂的柔软性和弹性,提高涂料涂抹后的柔软性。本专利技术中,以聚硅氧烷作为改性剂,以甲基丙烯酸缩水甘油酯、十二烷基苯磺酸钠乳化体系,形成的乳化体系稳定性好,成膜速度快,本专利技术中,过硫酸铵可与基 ...
【技术保护点】
一种纺织印花涂料粘合剂,其特征在于,其由质量份的以下原料组成:甲基丙烯酸甲酯20~40份、丙烯酸丁酯50~60份、过硫酸铵1~3份、甲基丙烯酸缩水甘油酯1~5份、十二烷基苯磺酸钠1~6份、辛基酚聚氧乙烯1~7份、丙烯腈1~8份、甲壳素1~5份、聚硅氧烷2~5份、甲醛捕捉剂0.1~3份、2,4‑二羟基二苯甲酮2~5份。
【技术特征摘要】
1.一种纺织印花涂料粘合剂,其特征在于,其由质量份的以下原料组成:甲基丙烯酸甲酯20~40份、丙烯酸丁酯50~60份、过硫酸铵1~3份、甲基丙烯酸缩水甘油酯1~5份、十二烷基苯磺酸钠1~6份、辛基酚聚氧乙烯1~7份、丙烯腈1...