The present invention provides an organic precursor of ZrC modified C/C composites with high thermal conductivity, the preparation method comprises the following steps: 1) ZrC organic precursor powder is evenly coated on the surface of C/C composites; 2) the tile C/C composite material to heat the mould; 3) will heat die into a molding machine. Fast heating up to 500 DEG C for heat molding; 4) was modified with C/C constant voltage insulation composite body after; 5) on the body by carbonization and graphitization. The ZrC organic precursor modified high heat conducting C/C composite material of the invention is a high thermal conductivity C/C composite with good thermal conductivity and high thermal conductivity.
【技术实现步骤摘要】
ZrC有机前驱体改性高导热C/C复合材料
本专利技术涉及一种ZrC有机前驱体改性高导热C/C复合材料，属于化工材料
技术介绍
C/C复合材料是指以炭纤维或其织物为增强相，以化学气相渗透的热解炭或液相浸渍－炭化的树脂炭、沥青炭为基体组成的一种纯炭多相结构。它源于1958年，美国Chance－Vought公司由于实验室事故，在炭纤维树脂基复合材料固化时超过温度，树脂炭化形成C/C复合材料。炭/炭（C/C）复合材料是一种新型高性能结构、功能复合材料，具有高强度、高模量、高断裂韧性、高导热、隔热优异和低密度等优异特性，在机械、电子、化工、冶金和核能等领域中得到广泛应用，并且在航天、航空和国防领域中的关键部件上大量应用。我国对C/C复合材料的研究和开发主要集中在航天、航空等高
，较少涉足民用高性能、低成本C/C复合材料的研究。整体研究还停留在对材料宏观性能的追求上，对材料组织结构和性能可控性、可调性等基础研究还相当薄弱，难以满足国民经济发展对高性能C/C复合材料的需求。因此，开展高性能C/C复合材料的基础研究具有重大的科学意义和社会、经济效益。国内在C/C复合材料研究方面历史较短,材料研究基本上处于探索阶段。
技术实现思路
本专利技术的目的是克服现有技术的不足之处，提供一种ZrC有机前驱体改性高导热C/C复合材料。本专利技术的ZrC有机前驱体改性高导热C/C复合材料，其制备方法包括如下步骤：1）将ZrC有机前驱体粉末均匀涂覆在C/C复合材料表面；2）将C/C复合材料平铺于耐热模具内；3）将耐热模具放入热压成型机中，快速升温至500℃进行热模压成型；4）恒...
【技术保护点】
ZrC有机前驱体改性高导热C/C复合材料，其特征在于，其制备方法包括如下步骤：1）将ZrC有机前驱体粉末均匀涂覆在C/C复合材料表面；2）将C/C复合材料平铺于耐热模具内；3）将耐热模具放入热压成型机中，快速升温至 500℃进行热模压成型；4）恒压保温得到改性后的C/C 复合材料坯体；5）对所得坯体进行炭化和石墨化处理。
【技术特征摘要】
1.ZrC有机前驱体改性高导热C/C复合材料，其特征在于，其制备方法包括如下步骤：1）将ZrC有机前驱体粉末均匀涂覆在C/C复合材料表面；2）将C/C复合材料平铺于耐热模具内；3）将耐热模具放入热压成型机中，快速升温至500℃进行热模压成型；4）恒压保温得到改性后的C/C复合材料坯体；5）对所得坯体进行炭化和石墨化处理。2.根据权利要求1所述的ZrC有机前驱体改性高导热C/C复合材料，其特征在于，所述的步骤3）中，快速升温的速...
【专利技术属性】
技术研发人员：朱爱民，
申请(专利权)人：南通市苏中纺织有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。