The invention discloses a new type of high performance cable material, belonging to the field of cable manufacture. It mainly consists of the following components according to the quality of parts of the preparation of phenolic resin: 20 copies, 10 copies of silicon carbide, low density polyethylene 10, stearic acid 2, magnesium hydroxide, zinc borate 2 copies, 1 copies, two methylamino ethoxyethanol 0.5, composite stabilizer 0.2, flame retardant 0.4. The invention has the advantages of low raw material, reasonable compatibility, good insulation property, high temperature resistance and corrosion resistance, good flame retardancy, and greatly improved safety factor. The invention is mainly used for making cables.
【技术实现步骤摘要】
一种新型高性能电缆材料
本专利技术属于电缆制作领域，具体地说，尤其涉及一种新型高性能电缆材料
技术介绍
电力电缆一般敷设在地表以下，与架空线相比，因其铺设在地表以下，所以受气候的影响较小，安全可靠，隐蔽耐用，但是材料成本、敷设费用、维护费用比较高，而且检修和故障排查也比较困难。低压配电网、电气设备用电线电缆常采用具有聚氯乙稀护套的塑料外皮电线作为电能传输线，这些电线一般通过穿管埋设在墙体或地表下。电线的绝缘不良产生的火花往往容易引起厂房、住宅、公共场所等处火灾，造成人员伤亡和财产损失。
技术实现思路
本专利技术的目的在于克服上述缺陷，提供一种新型高性能电缆材料，其原料低廉、配伍合理，绝缘性能好，耐高温、耐腐蚀，具有良好的阻燃性。所述的新型高性能电缆材料，由按质量份计的下述成分制备的：酚醛树脂20份，碳化硅10份，低密度聚乙烯10份，硬脂酸2份，氢氧化镁2份，硼酸锌1份，二甲氨基乙氧基乙醇0.5份，复合稳定剂0.2份，阻燃剂0.4份。与现有技术相比，本专利技术的有益效果是：本专利技术原料低廉、配伍合理，绝缘性能好，耐高温、耐腐蚀，具有良好的阻燃性，大大提高了安全系数。具体实施方式下面结合实施例对本专利技术作进一步说明：新型高性能电缆材料，由按质量份计的下述成分制备的：酚醛树脂20份，碳化硅10份，低密度聚乙烯10份，硬脂酸2份，氢氧化镁2份，硼酸锌1份，二甲氨基乙氧基乙醇0.5份，复合稳定剂0.2份，阻燃剂0.4份。本专利技术的制备方法如下：按照重量比例取各原料，倒入高速搅拌机中，室温下先以800转/分钟的速度搅拌混合30min，然后在60℃下以4500转/分钟...
【技术保护点】
一种新型高性能电缆材料，其特征在于：所述套管是由按质量份计的下述成分制备的：酚醛树脂20份，碳化硅10份，低密度聚乙烯10份，硬脂酸2份，氢氧化镁2份，硼酸锌1份，二甲氨基乙氧基乙醇0.5份，复合稳定剂0.2份，阻燃剂0.4份。
【技术特征摘要】
1.一种新型高性能电缆材料，其特征在于：所述套管是由按质量份计的下述成分制备的：酚醛树脂20份，碳化硅10份，低密度...
【专利技术属性】
技术研发人员：李春花，
申请(专利权)人：青岛祥智电子技术有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。