The invention provides a low temperature corrosion inhibitor for circulating water, which comprises zinc salt, organic phosphonic acid salt, inorganic phosphonate, dispersing agent and deionized water. The present invention can generate a kind of impermeable protective film with reticular structure on the surface of metal, which can inhibit the corrosion of iron, so as to prevent corrosion. In addition, the low temperature corrosion inhibitor of the circulating water has the property of scale inhibition at the same time, can reduce the deposition of calcium carbonate on the wall of the heat exchanger and reduce the deposition of calcium sulfate in water.
【技术实现步骤摘要】
本专利技术属于循环水专用药剂,特别涉及一种用于循环水的低温缓蚀剂。
技术介绍
在工业循环水中,制氧循环冷却水系统有着其特殊性,因系统中有空气预冷设备,主要表现在空冷塔和冷冻机组处于低温运行状态,温度为5℃左右,循环冷却水经过该类设备时,水温下降,引起水中离子溶解度减低而从水中析出,附着在设备表面,易导致设备腐蚀,影响换热效果。因此,需要加入缓蚀剂来抑制腐蚀现象。本专利技术提供的循环水低温缓蚀剂,能够在金属表面与铁离子或氧化铁反应生成一种网状结构的不透性保护膜,能抑制铁的腐蚀,从而起到缓蚀功能。另外,本循环水低温缓蚀剂同时还具有阻垢的性能,能够减少碳酸钙在热交换器管壁上的沉积以及能够减少水中硫酸钙的沉积。
技术实现思路
本专利技术的目的在于提供一种循环水低温缓蚀剂;具有良好的缓蚀效果;对碳酸钙、硫酸钙等多种垢具有优良的抑制作用和良好的分散作用。同时,该缓蚀剂组分简单、原料易得、成本低廉、毒性低。本专利技术所采用的技术方案如下:一种循环水低温缓蚀剂,含有锌盐、有机膦酸盐、无机膦酸盐、分散剂和去离子水。各组分的重量百分比为:去离子水 30~80%锌盐 1~10%无机膦酸盐 1~10%有机膦酸盐 5~25%分散剂 10~30%。所述的锌盐为硫酸锌、氯化锌、氧化锌中的一种或几种。所述的有机膦酸盐为羟基亚乙基二膦酸、2-膦酸基-1,2,4-三羧酸丁烷、乙二胺四亚甲基膦酸、氨基三亚甲基膦酸中 ...
【技术保护点】
一种循环水低温缓蚀剂,含有锌盐、有机膦酸盐、无机膦酸盐、分散剂和去离子水。
【技术特征摘要】
1.一种循环水低温缓蚀剂,含有锌盐、有机膦酸盐、无机膦酸盐、分散剂和去离子水。2.根据权利要求1所述循环水低温缓蚀剂,各组分的重量百分比为:去离子水 30~80%锌盐 1~10%无机膦酸盐 1~10%有机膦酸盐 5~25%分散剂 10~30%。3.所述的锌盐为硫酸锌、氯化锌、氧化锌中的一种或几种。4.所述的有机膦酸盐为羟基亚乙基二膦酸、2-膦酸...
【专利技术属性】
技术研发人员:陈维忠,李洪社,喻果,
申请(专利权)人:威海翔宇环保科技股份有限公司,
类型:发明
国别省市:山东;37