一种制备太阳能电池表面反射膜涂层喷涂新配方组成比例

一种制备太阳能电池表面反射膜涂层喷涂新配方，本发明专利技术涉及一种用常压化学蒸汽淀积法喷涂太阳能电池表面反射膜涂层的新配方，其特征在于：所述配方由钛酸四丁酯、乙酸正丁酯、异辛醇组成，其重量百分比为：钛酸四丁酯70％，乙酸正丁酯15％，异辛醇15％。通过本发明专利技术涉及的配方，可以增加二氧化钛膜的厚度和增强二氧化钛膜的致密性，改善膜层各个方向的视差，实用且美观，对太阳能的吸收效果好，能量转化效率高。

Novel formulation for preparing surface reflection film coating of solar cell

A preparation of reflective solar cell surface coating spraying formula, the invention relates to a new formula by atmospheric pressure chemical vapor deposition method spraying reflective solar cell film on the surface of the coating, which is characterized in that the formula consists of four butyl titanate, butyl acetate, ISO octyl alcohol group, its weight percentage: four titanate 70% butyl acrylate, butyl acetate 15%, isooctyl alcohol 15%. The invention relates to a formulation that can increase the TiO2 film thickness and enhance the compactness of TiO2 film, improve the film parallax in every direction, practical and beautiful, the absorption efficiency of solar energy, high energy conversion efficiency.

【技术实现步骤摘要】

【技术保护点】
一种用常压化学蒸汽淀积法制备太阳能电池表面反射膜涂层的新配方，其特征在于：所述配方由钛酸四丁酯、乙酸正丁酯、异辛醇组成，其重量百分比为：钛酸四丁酯70％，乙酸正丁酯15％，异辛醇15％。

【技术特征摘要】

【专利技术属性】
技术研发人员：沈华江，
申请(专利权)人：上海佳途太阳能科技股份有限公司，
类型：发明
国别省市：