The ceramic coating and the preparation method of the invention relates to an anti sea biological corrosion, which belongs to the technical field of ceramics, the weight of each component for the Magnesium Oxide 15-30, 50-70, 5-20 silica alumina, Zinc Oxide 2-20, the preparation method of the components at 800-1500 DEG C high temperature burning 30-100min, remove the cooling at room temperature, the ceramic coating anti sea biological corrosion; the ceramic coating not only keeps the ceramic coating abrasion resistance, high temperature, antioxidant and other original characters, at the same time due to the addition of alumina can significantly improve the performance of marine corrosion resistance coating, expanding the application of ceramic coating in ship parts.
【技术实现步骤摘要】
本专利技术涉及一种抗海生物腐蚀的陶瓷涂层,具体涉及,属于陶瓷生产
。
技术介绍
随着海上交通的发展,船舰的维修保养工作占航海成本的比例逐渐提高,如何降低船舰的维修保养费用是各航海企业目前面临的主要问题之一。在所有船舰维修工作中,船舰零部件因海水腐蚀而需要维修护理的现象尤为突出,并占据维修费用的最大比例。船舰长年累月浸泡在海水中,不可避免被海水和海上微生物腐蚀,导致零部件不同程度的损坏,所以研究开发一种抗海生物腐蚀的材料,保护船舰零部件,延长器使用寿命,是非常有意义的。陶瓷是将一定的原料组成,经高温灼烧然后冷却而成,具有不可溶性、稳定性等特质。通过添加抗海生物腐蚀的原料,改良陶瓷特性,研制一种抗海生物腐蚀的陶瓷,经胶黏剂附在船舰零部件上,不仅保持陶瓷涂层耐磨、耐高温、抗氧化等原有特性,同时由于抗海生物腐蚀的原料的加入显著提高了涂层的抗海生物腐蚀性能,扩大了陶瓷涂层在舰船零部件上的应用。目前关于抗海生物腐蚀的陶瓷涂层的专利仅有一个,201110100223.1公开,其特征在于其涂层为由氧化铜颗粒弥散分布于陶瓷基体中形成的复合陶瓷涂层,由于某些技术仍未突破,所以该专利不被授权。所以在国内,抗海生物腐蚀的陶瓷涂层 的专利仍未有申请。航海运输是我国重要的交通运输方式之一,也是世界上重要的运输方式,研究开发一种抗海生物腐蚀的陶瓷涂层,延长船舰零部件的寿命,降低航海船只的维修成本有着重要意义。
技术实现思路
本专利技术的目的是提供一种抗海生物腐蚀的陶瓷涂层;该陶瓷涂层不仅保持了陶瓷涂层耐磨、耐高温、抗氧化等原有特性,同时由于氧化铝的加入显著提高了涂层 ...
【技术保护点】
一种抗海生物腐蚀的陶瓷涂层,其特征在于:各组分的重量份为:氧化镁15?30份、氧化铝50?70份、二氧化硅5?20份、氧化锌2?20份。
【技术特征摘要】
1.一种抗海生物腐蚀的陶瓷涂层,其特征在于:各组分的重量份为: 氧化镁15-30份、氧化铝50-70份、二氧化硅5-20份、氧化锌2_20份。2.根据权利要求1所述的一种抗海生物腐蚀的陶瓷涂层,其特征在于:所述的氧化铝采用质量含量为95%的氧化铝。3.一种用于制备权利要求1所述的抗海生物腐蚀的陶瓷涂层的方法,...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。