The present invention relates to a wood plastic composite material can be electromagnetic shielding, which is characterized in that the preparation method of recycling PP broken to 0.1 ~ 0.7cm in diameter and the particle crushing of wood fiber to 40 ~ 120 mesh; then 30-60 resin, 40-50 wood powder, graphite powder, 10-15 parts of a lubricant, a compatible 3-5 3-6 a 2-3 agent, dispersing agent are added high speed mixing 30-60min mixing machine, the components are mixed thoroughly, it will finally premix premixed powder; extrusion granulation and forming. Advantages: will the graphite powder ingredients into effect of electromagnetic shielding wood system using special technology, wood plastic composite material has the function of electromagnetic shielding.
【技术实现步骤摘要】
本专利技术涉及一种塑木复合材料的制备方法,具体涉及一种可屏蔽电磁的塑木复合材料的制备方法。
技术介绍
塑木复合材料是一种兼具木材与塑料两者优点的复合材料,其节能环保、木质感强,受热稳定不易变形,无有害气体,但是由于自身的性能单一性,其应用仅仅局限于户外地板、护栏、廊桥等。
技术实现思路
本专利技术旨在克服现有塑木复合材料应用范围狭窄,提出一种可屏蔽电磁的塑木复合材料的制备方法。本专利技术的技术解决方案:首先将回收PP破碎至直径0.1 0.7cm的粒子和粉碎木纤维至40 120目;再将30-60份树脂、40-50份木粉、10-15份石墨粉、3_6份润滑剂、3_5份相容剂、2-3份分散剂依次加入高速混料机中混合30-60min,待各组分充分混合后,得预混料;最后将预混料挤出造粒和成型。本专利技术的有益之处在于:采用专门的工艺将起屏蔽电磁作用的石墨粉成份融合进塑木体系,塑木复合材料具有屏蔽电磁的功能。具体实施例方式首先将回收PP破碎至直径0.2cm的粒子和粉碎木纤维至60目;再将40KG树脂、45KG木粉、12KG石墨粉、4KG硬脂酸镁、4KG相容剂、2KG分散剂依次加入高速混料机中混合50min,待各组分充分混合后,得预混料;最后将预混料挤出造粒和成型,即可得到本专利技术产品。权利要求1.一种可屏蔽电磁的塑木复合材料,其特征在于其制造工艺如下:首先将回收PP破碎至直径0.1 0.7cm的粒子和粉碎木纤维至40 120目;再将30-60份树脂、40-50份木粉、10-15份石墨粉、3-6份润滑剂、3-5份相容剂、2-3份分散剂依次加入高速混料机中混合30-60mi ...
【技术保护点】
一种可屏蔽电磁的塑木复合材料,其特征在于其制造工艺如下:首先将回收PP破碎至直径0.1~0.7cm的粒子和粉碎木纤维至40~120目;再将30?60份树脂、40?50份木粉、10?15份石墨粉、3?6份润滑剂、3?5份相容剂、2?3份分散剂依次加入高速混料机中混合30?60min,待各组分充分混合后,得预混料;最后将预混料挤出造粒和成型。
【技术特征摘要】
【专利技术属性】
技术研发人员:陈璟,吴光荣,吕延,
申请(专利权)人:南京荣仕景复合材料有限公司,
类型:发明
国别省市: