The invention discloses a method for synthesizing rubber additives NS, it includes the steps of the synthesis of accelerator M by ammonia dissolved after the formation of M NH4, then M and NH4 reaction of TERT butylamine, reaction product by filtration, washing, drying and sieving the generation of rubber additives NS, tert butylamine and M NH4 reaction steps: TERT butylamine and M NH4 were put into liquid oxidation reactor, mixing evenly, under stirring, adding catalyst of copper acetate and lead sulfate, amount of the catalyst for the quality of accelerator M 0.02 - 0.04%, and then pass into the oxygen, the temperature is 30 to 40 DEG C under the condition of the reaction is 1 to 3 hours. The invention adopts green oxygen oxidizing agent, inorganic salt product does not contain water, less water consumption, saving 2 / 3 process water, the process is simple and easy to industrialization, excellent environmental protection, energy saving, safety.
【技术实现步骤摘要】
本专利技术属于橡胶助剂的生产
,具体涉及一种橡胶助剂NS的合成方法。NS(N_叔丁基-2-苯并噻唑次磺酰胺)是天然橡胶、顺丁橡胶、异戊橡胶、丁苯橡胶 和天然再生胶的迟延性促进剂。用于高中档轿车子午线轮胎,与食品接触的橡胶制品以及 医用橡胶制品。用途极为广泛。NS在制造及使用过程中不会产生亚硝胺,被业界称作环保 型促进剂,是一个很有发展前途的产品。目前,NS的合成方法是以促进剂M(2-硫醇基苯骈 噻唑)、叔丁胺为原料,次氯酸钠为氧化剂,采用水相合成方法,但是此合成方法排放大量的 含盐废水,而且很难处理,对环境污染严重。
技术实现思路
本专利技术要解决的技术问题是橡胶助剂NS的合成方法以次氯酸钠为氧化剂而排放 大量的含盐废水,处理时不易处理并且耗水量大,提供一种以氧气为氧化剂,醋酸铜和硫酸 铅为催化剂的橡胶助剂NS的合成方法。本专利技术的技术方案是一种橡胶助剂NS的合成方法,它的合成步骤包括将促进剂 M用氨水溶解后,生成M-NH4,然后将叔丁胺与M-NH4K应,反应产物经抽滤、水洗、干燥、过筛 生成橡胶助剂NS,所述叔丁胺与M-NH4反应的步骤是将叔丁胺与M-NH4液体分别投入氧化 釜中,混合均勻后,在搅拌状态下,加入催化剂醋酸铜和硫酸铅,催化剂的加入量为促进剂M 的质量的0. 02-0. 04%,然后通入氧气,在温度为30 40°C的条件下,反应1 3小时。所述叔丁胺与M-NH4的物质的量之比为1. 2 1. 6 1,优选为1. 45 1。所述催化剂醋酸铜和硫酸铅的质量比为8 10 1,优选为9 1。本专利技术的反应原理(1)将促进剂M用氨水 ...
【技术保护点】
1.一种橡胶助剂NS的合成方法,它的合成步骤包括将促进剂M用氨水溶解后,生成M-NH4,然后将叔丁胺与M-NH4反应,反应产物经抽滤、水洗、干燥、过筛生成橡胶助剂NS,其特征在于:所述叔丁胺与M-NH4反应的步骤是:将叔丁胺与M-NH4液体分别投入氧化釜中,混合均匀后,在搅拌状态下,加入催化剂醋酸铜和硫酸铅,催化剂的加入量为促进剂M的质量的0.02-0.04%,然后通入氧气,在温度为30~40℃的条件下,反应1~3小时。
【技术特征摘要】
【专利技术属性】
技术研发人员:张智亮,陈建军,
申请(专利权)人:鹤壁联昊化工有限公司,
类型:发明
国别省市:41[中国|河南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。