The invention provides a dye sensitized solar cell composite light anode, which belongs to the technical field of functional materials and devices, and relates to dye sensitized solar cells. Composite photoanode is provided comprising conductive glass, titanium oxide transition layer and TiO2 modified layer; the titanium oxide transition layer by using titanium dioxide slurry prepared by hydrothermal method coated on conductive glass surface of the conductive layer and after drying and sintering; the composite TiO2 modified TiO2 layer using mixed slurry coating in the transition layer on the surface of titanium dioxide and after drying and sintering; the titanium dioxide mixed slurry by using TiO2 slurry prepared by hydrothermal method with the template prepared TiO2 hollow microspheres mixture, wherein the hollow titania microspheres doped with 10% to 40% silver, between 400 to 1000 nm in diameter. The dye-sensitized solar cell composite light anode provided by the invention has higher photoelectric conversion efficiency.
【技术实现步骤摘要】
本专利技术属于功能材料及器件
，涉及染料敏化太阳能电池，尤其涉及染料敏化太阳能电池光阳极结构及其制备方法。
技术介绍
染料敏化太阳能电池的结构通常是一种由吸附了敏化染料的TiO2光阳极、电解质和对电极组成的三明治结构，英文简称为DSSC。由于DSSC的制作工艺简单、成本低廉、以及对环境友好等特点使其成为替代传统无机太阳能电池的很有潜力的候选者。自从1991年瑞士洛桑高工的Gratzel将DSSC的光电转换效率做到7. 1 %以来，各国科学家纷纷投入大量的精力研究DSSC各种可喜的成果也不断涌现；科学家一度将DSSC的光电转换效率做到了 11%以上。在DSSC中，各部分的性能都会对电池的光电转换效率有重要影响，其中TW2光阳极的结构和性能是对DSSC光电转换效率产生较大影响的关键因素。目前对DSSC的TiO2光阳极的改性主要集中在对二氧化钛膜的修饰上，通过对二氧化钛膜的表面改性以增加二氧化钛膜对染料的吸附量、降低二氧化钛与电解液之间的界面电阻、延长光生载流流子在二氧化钛膜中的寿命，从而提高整个电池的光电转换效率。 Chou 等(Powder Technol....
【技术保护点】
１．一种染料敏化太阳能电池复合光阳极，包括导电玻璃、位于导电玻璃导电层（２）上的二氧化钛过渡层（３）和二氧化钛过渡层（３）表面的复合二氧化钛改性层（４）；所述二氧化钛过渡层（３）厚度在４～７微米之间，由采用水热法制备的二氧化钛浆料刮涂于导电玻璃的导电层（２）表面并经烘干、烧结而成；所述复合二氧化钛改性层（４）的厚度在３～５微米之间，采用二氧化钛混合浆料刮涂于二氧化钛过渡层（３）表面并经烘干、烧结而成；所述二氧化钛混合浆料由采用水热法制备的二氧化钛浆料与采用模板法制备的二氧化钛空心微球混合而成，其中二氧化钛空心微球掺有１０％至４０％的银、直径在４００～１０００纳米之间。
【技术特征摘要】
【专利技术属性】
技术研发人员：贾春阳，李孜，郝贵敏，万中全，
申请(专利权)人：电子科技大学，
类型：发明
国别省市：90