The invention discloses a hydrometallurgical high acid leaching of low pollution jarosite neutralization process, including neutral leaching, low temperature and high temperature and high acid leaching, and low pollution jarosite iron four process, which is characterized in that the low pollution jarosite iron removal step, the temperature of pre neutralization with liquid overflow ammonium bicarbonate, sodium bicarbonate and cadmium smelting slag, so that ferric ions in solution is not dissolved in sulfuric acid, and dissolved easily jarosite crystal precipitation, washing and filtering and settling down, jarosite after fluid neutral leaching. Using cadmium smelting slag instead of partial caustic soda and ammonium bicarbonate as neutralization agent and precipitating agent, not only can better process result be obtained, but also valuable metals such as zinc and cadmium in cadmium smelting slag have been recovered.
【技术实现步骤摘要】
本专利技术涉及有色金属冶炼
，尤其是涉及一种湿法炼锌高酸浸出低污染沉 矾中和工艺。
技术介绍
随着湿法炼锌工艺的快速发展，高酸浸出-低污染沉矾工艺在国内外得到快速发 展。如本公司申请的专利技术专利CN100374592C“一种低污染沉矾除铁湿法炼锌方法”，该方法 主要包括中性浸出、低温预中和、高温高酸浸出和低污染沉矾除铁四个工艺步骤，在低污染 沉矾除铁之前，先通过高温高酸浸出，将铁最大限度地浸出出来，然后通过低温预中和调整 溶液的组成，最后将预中和溢流液加入烧碱、碳酸钠、氢氧化钠、碳酸氢铵或其混合物，其主 要反应式为3Fe2 (SO4) 3+10H20+2NH40H = (NH4) 2Fe6 (SO4) 4 (OH) 12+5H2S043Fe2 (SO4) 3+12H20+Na2S04 = Na2Fe6 (SO4) 4 (OH) 12+6H2S04通过上述化学反应式看出，溶液中的三价铁离子生成为既不溶解于硫酸，又溶易 沉淀、洗涤和过滤的黄钾铁矾晶体而沉淀下来，同时，随着铁矾的生成，反应过程相应地水 解出硫酸。根据铁矾生成条件，酸度提高不利于铁矾的生成，所以...
【技术保护点】
一种湿法炼锌高酸浸出低污染沉矾中和工艺，包括中性浸出、低温预中和、高温高酸浸出和低污染沉矾除铁四个工艺步骤，其特征在于：在低污染沉矾除铁步骤中，加入低温预中和的溢流液、碳酸氢铵、碳酸氢钠和镉熔炼渣，让溶液中的三价铁离子成为既不溶解于硫酸，又溶易沉淀、洗涤和过滤的黄钾铁矾晶体而沉淀下来，沉矾后液返中性浸出。
【技术特征摘要】
【专利技术属性】
技术研发人员：王凤朝，李龙，马永涛，张春明，曹延峰，冯国军，曹猛，朱永良，关旭东，孙晓军，肖常玲，
申请(专利权)人：赤峰中色库博红烨锌业有限公司，
类型：发明
国别省市：15