一种轻质化改造的主铁沟浇注料制造技术

技术编号:6064666 阅读:229 留言:0更新日期:2012-04-11 18:40
本发明专利技术公开了一种轻质化改造的主铁沟浇注料,所述浇注料由矾土、棕刚玉、SiC、SiO2微粉、α-Al2O3微粉、球状沥青、氧化铝空心球、防爆纤维、金属硅粉、红柱石精矿粉、铝酸钙水泥、三聚磷酸钠组成。本发明专利技术采用在主铁沟料里面引入氧化铝空心球,对传统重质耐火材料铁沟料进行轻质化改造,其推广应用不仅可以为用户降低耐火材料消耗,对促进高温设备的保温、节能亦有利。因为氧化铝空心球的加入,使产品的体积密度降低,导热系数降低,达到了对主铁沟浇注料保温的效果。

Main iron groove castable for light weight modification

The main iron trough castable of the invention discloses a method of changing light, the castable is composed of bauxite, Zong Gangyu, SiC, SiO2 powder, -Al2O3 powder, asphalt, spherical alpha alumina hollow ball, explosion-proof fiber, metal powder, andalusite powder, calcium aluminate cement, sodium tripolyphosphate. The invention adopts the introduction of alumina hollow ball in the main iron runner, light of the transformation of traditional heavy refractory ferrous material, its application can not only for users to reduce the consumption of refractory material, also beneficial to promote energy-saving insulation, high temperature equipment. Because the alumina hollow ball is added, the volume density of the product is reduced, and the thermal conductivity is reduced, and the effect of the heat preservation of the main iron channel castable is achieved.

【技术实现步骤摘要】

本专利技术涉及一种耐火浇注料。
技术介绍
现有主铁沟浇注料都是特重质浇注料。高炉的炉况,原材料的品位,烧结矿的好 坏,以及设备原因都会造成高炉的休风检修。往往休风检修对高炉主铁沟通铁量影响巨大。 影响原因有许多原因。其中有很大一部分原因由如下两条造成的。1,保温性能差。特别是高炉休风时,保温性能差,需要在主铁沟里面插3-4根简易 煤气管来保温,但即使这样,保温效果依然不佳。这样容易导致因为温度下降而产生的裂 纹。2,抗热震稳定性能差。一旦休风,主铁沟沟边容易出现5mm以上的裂纹,影响通铁量。
技术实现思路
本专利技术所要解决的技术问题就是提供一种主铁沟浇注料,使产品的体积密度降 低,导热系数降低,提高主铁沟浇注料的抗热震稳定性。为解决上述技术问题,本专利技术采用如下技术方案一种轻质化改造的主铁沟浇注 料,其特征在于所述浇注料由矾土、棕刚玉、Sic、SiO2微粉、α-Al2O3微粉、球状浙青、氧化 铝空心球、防爆纤维、金属硅粉、红柱石精矿粉、铝酸钙水泥、三聚磷酸钠组成。优选的,所述浇注料中各组分的重量百分比为矾土 10% 15% ;棕刚玉45% 50% ;SiC10% 15% 微粉 本文档来自技高网...

【技术保护点】
1.-种轻质化改造的主铁沟浇注料,其特征在于:所述浇注料由矾土、棕刚玉、SiC、SiO2微粉、α-Al2O3微粉、球状沥青、氧化铝空心球、防爆纤维、金属硅粉、红柱石精矿粉、铝酸钙水泥、三聚磷酸钠组成。

【技术特征摘要】

【专利技术属性】
技术研发人员:佘成其马少杰
申请(专利权)人:佘成其
类型:发明
国别省市:33