锂二次电池用正极活性物质及其制造方法以及锂二次电池技术

本发明专利技术提供锂二次电池用正极活性物质及其制造方法以及锂二次电池。具体来说，本发明专利技术在于得到由含有作为过渡金属的Mn、且具有层状结构、过量含有锂的含锂过渡金属氧化物形成的放电容量高的锂二次电池用正极活性物质及其制造方法以及使用其的锂二次电池。使用一种锂二次电池用正极活性物质，其是以通式Li1+xMn1-x-yMyO2(此处,x和y为0＜x＜0.33、0＜y＜0.66的范围，M表示除Mn以外的至少一种过渡金属。)表示、且具有层状结构的含锂过渡金属氧化物，其表面形成有氧化硼层。

Positive electrode active material for lithium secondary battery and manufacturing method thereof, and lithium two cell two

The present invention provides a positive electrode active material for a lithium two cell, a method for manufacturing the same, and a lithium two cell. Specifically, the present invention is obtained by containing transition metals as Mn, and has two lithium battery discharge capacity, excess layered lithium containing lithium containing transition metal oxide formed with high cathode active material and method of manufacturing and using the lithium secondary battery two. Using a positive electrode active material for a lithium two cell, the M represents at least one transition metal other than Mn in the range Li1+xMn1-x-yMyO2, x, y, 0, x < 0.33, 0 < y < 0.66. A lithium containing transition metal oxide having a layered structure and having a boron oxide layer formed on its surface.

【技术实现步骤摘要】

本专利技术涉及由含有作为过渡金属的Mn、过量含有Li、且具有层状结构的含锂过渡金属氧化物形成的锂二次电池用正极活性物质及其制造方法以及使用其的锂二次电池。
技术介绍
已知以Li1+xMni_x_yMy02(此处，M为除Mn以外的至少一种过渡金属。)表示的Li量过剩的Mn系层状活性物质显示200mAh/g以上的放电容量(例如非专利文献1)。与含有1 摩尔Li的LiCoA等现有活性物质相比，该活性物质这样含有1+x摩尔Li的活性物质在理论上应该能够显示较高的放电容量。然而，尽管含有过量的Li，但仍未能获得高放电容量。本专利技术人为了改善放电容量而研究对该活性物质设置被覆层。对于在活性物质的表面设置被覆层，已知有如下现有技术。在专利文献1和非专利文献2中，提出了通过用锂硼氧化物对LiMn2O4进行表面处理来改善高温保存特性，但在另一方面放电容量有所降低。可认为这是由于因设置被覆层而使表面积减小、使电极与电解液之间的反应减少。在专利文献2中，公开了在LiCoA中添加化03来使保存时的Co的溶解减少、使自放电减少。在专利文献3中，公开了通过将MnO2或Li-Mn化合物(Mn Li = 7 本文档来自技高网...

【技术保护点】
１．一种锂二次电池用正极活性物质，其特征在于，其是以通式Ｌｉ１＋ｘＭｎ１－ｘ－ｙＭｙＯ２表示、且具有层状结构的含锂过渡金属氧化物，且其表面形成有氧化硼层，式中，ｘ和ｙ为０＜ｘ＜０．３３、０＜ｙ＜０．６６的范围，Ｍ表示除Ｍｎ以外的至少一种过渡金属。