The invention relates to a method for coating internal pipe joint, which comprises the following steps: 1) cleaning pipe joint; 2) the shielding sleeve is screwed in the rubber pipe joint internal thread part, wherein the rubber sheath comprises an annular flange portion of the hollow cylindrical shield and shield section along the cylindrical end to extend toward the outer diameter ring, side of the cylindrical shielding part with an external thread and the joint internal thread part matched with the pipe joint; 3) heating; 4) with spray PVC dip liquid spray evenly to the inner surface of the pipe joint PVC dip coating liquid layer is formed on the inner surface of pipe joint; 5) the inner surface of the pipe joint vulcanization PVC dip coating liquid; 6) cooling pipe joints, remove the rubber sheath; 7) inspection, packaging and storage. The invention reduces the cost of coating, and can avoid the external pipe joint and the internal thread part is coated with a coating of pipe conveying medium so as to avoid the pollution caused by.
【技术实现步骤摘要】
本专利技术涉及一种管接头涂塑方法，尤其涉及对管接头内部进行涂塑的方法。
技术介绍
管接头内部通常需要经过涂塑来进行防腐蚀处理，现有的涂塑方法主要有三种， 即液态浸塑方法、粉状涂塑方法和内衬涂塑方法。液态浸塑方法包括以下步骤1)管接头清洗；2)采用燃料热风道或工业电加热炉 对管接头加热，加热时间为20分钟，加热温度220°C ；3)将管接头放入液态涂料中进行浸 塑，浸塑时间为2分钟；4)取出管接头，放入燃料热风道或工业电加热炉进行加热硫化，硫 化时间为10分钟，硫化温度为180°C;5)取出管接头自然冷却至常温；6)检验、包装。现有 的这种液态浸塑方法对管接头进行的是内外包覆涂塑，其材料耗用大及材料成本高；并且 管接头在浸塑时，管接头的内螺纹部位也被涂有涂料，在管接头安装使用时，管接头内螺纹 部的涂料在连接拧紧过程中被挤压掉，被挤压掉的涂塑材料全部掉入管接头中，对管件内 的输送介质造成污染。采用粉状涂塑方法对管接头进行涂塑后，管接头的内螺纹部位同样 也被涂有涂料。为了解决管接头的外部以及内螺纹部被涂上涂料的问题，出现了内衬涂塑方法， 其包括以下步骤1)管接头清洗...
【技术保护点】
一种管接头内部涂塑方法， 其特征在于，包括以下步骤：１）清洗管接头；２）将橡胶屏蔽套旋入到管接头的内螺纹部，所述橡胶屏蔽套包括中空的圆柱形屏蔽部和沿圆柱形屏蔽部的一端朝外径向延伸的环状凸缘部，圆柱形屏蔽部的环侧面设有与所述管接头内螺纹部相配合的外螺纹，圆柱形屏蔽部的环侧面的外螺纹与管接头的内螺纹部紧密贴合以将管接头的内螺纹部完全遮掩；３）将管接头加热；４）用喷枪将ＰＶＣ浸塑液均匀的喷涂到管接头的内表面，在管接头的内表面形成ＰＶＣ浸塑液涂层；５）硫化管接头内表面的ＰＶＣ浸塑液涂层；６）冷却管接头，卸掉橡胶屏蔽套；７）检验、包装入库。
【技术特征摘要】
【专利技术属性】
技术研发人员：唐光炳，
申请(专利权)人：四川金易管业有限公司，
类型：发明
国别省市：51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。