The invention relates to a waterproof material, in particular to a substitute for spraying waterproof material and its preparation method of wide polyurea waterproofing coating, spraying polyurea waterproof coating construction and solve the problems of higher cost of the existing formula, by chlorinated polyethylene, filling reinforcing agent, softening agent, phenolic antioxidant, heat stabilizer,. Light stabilizer and lubricant, mixing, mixing various raw materials; followed by plastic refining machine, open mill and granulator granulation; the pellets into a single screw extruder and the die forming; forming materials will invest three roller calender roll cooling press waterproofing membrane. Elongation, resilience has waterproof rubber coil softness and high, and keep the plastic type waterproof material with high tensile strength, more than the construction of spray polyurea waterproofing coating using the standard, and the production cost is low, has good application prospects.
【技术实现步骤摘要】
本专利技术涉及一种可以替代喷涂聚脲防水涂料的宽幅的新型防水卷材，具体为一种氯化聚乙烯防水卷材及其制备方法。
技术介绍
二十一世纪的建筑业已进入一个突飞猛进的发展时代，要求建筑物美观、耐用，建筑防水材料也必须具备重量轻、强度高、使用寿命长的特点。目前，混凝土防水层是提高建筑结构耐久性的重要技术手段，由于防水失效造成桥面或屋面渗水、钢筋锈蚀的事例很多， 直接影响了其使用寿命。目前高速铁路桥梁上应用最广泛的防水材料是喷涂聚脲防水涂料，它是一种聚脲弹性体，该技术将新材料、新设备和新工艺有机的结合在一起，是传统施工技术的一次革命性飞跃，是目前国际上最先进的施工技术之一。大量采用了喷涂聚脲防水方式，有效地解决了底座板下需设置连续防水的要求，但是其在应用过程中，也发现存在一些问题①工程造价高。聚脲材料费单价约90 120元/m2，施工费用高，单价约70-100 元/m2，合计为160-220元/m2。②影响因素多。为了达到良好的使用效果，喷涂聚脲防水涂料在施工过程中，对外界环境温度、湿度以及施工人员的操作技术有一定的要求。③聚脲喷涂施工要求一次性完全覆盖桥面，后续工序必然会对...
【技术保护点】
１．一种可以替代喷涂聚脲防水涂料的宽幅的新型防水卷材是由下列重量份数的原料制成：氯化聚乙烯９０－１２０份，填充增强剂２－３０份，软化增塑剂１０－４５份，酚类抗氧剂０．１－２份，热稳定剂３－１０份，光稳定剂０．４－１．５份，润滑剂３－８份，其他助剂０．５－３份；所述的氯化聚乙烯中氯含量为２５－４５ｗｔ％；所述的酚类抗氧剂由重量比为３５％的酚类主抗氧剂１０７６和６５％的辅助抗氧剂ＤＳＴＤＰ制成；所述的热稳定剂由６０％的三盐基硫酸铅和４０％复合热稳定剂制成。
【技术特征摘要】
【专利技术属性】
技术研发人员：牛斌，王保良，胡所亭，马林，魏峰，刘永建，葛凯，马美琴，修磊，王浩，鲍新艳，
申请(专利权)人：中国铁道科学研究院铁道建筑研究所，衡水新陆交通器材有限公司，
类型：发明
国别省市：11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。