The invention discloses a steel wire mesh autoclaved aerated concrete slabs, including steel mesh skeleton in aerated concrete slab in aerated concrete plate and lining; composed of reticular structure formed by the steel wire mesh and several wire, the wire diameter of 1.5-3.0 mm. As the steel wire of the invention adopts the autoclaved aerated concrete slabs reinforced more than thin wire, unit area reduced by nearly 4 times, and the use of dispersed reinforcement structure, the form of reinforcement is more reasonable, so the structure is more stable, more uniform and reasonable stress condition, can significantly improve the load strength, superior performance, and the manufacturing cost is low.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料，尤其涉及一种可用作建筑物墙体、屋面、隔层的钢丝网 蒸压加气混凝土板。
技术介绍
加气混凝土制品是以粉煤灰、石英砂及其尾矿等硅质材料和石灰、水泥等钙质材 料，经化学发气方法形成多孔结构，通过蒸压养护获得强度的新型建筑材料。它具有利废、 节能保温、质轻、环保等诸多优点，是一种绿色新型建材。加气混凝土制品分为砌块和板材 两种形式，其中板材又可以根据性能特点和用途分为墙板、屋面板和楼板。加气混凝土板材 主要是由各种形式的内衬钢筋骨架构成，其中的钢筋骨架包括单张网片、上下两张网片等 形式，目前国内基本都采用上下网片组合的结构(见图1)。如图2所示，现有钢筋骨架的钢 筋网片一般由横筋1、纵筋2焊接(焊点幻而成，采用4根横筋1，2根纵筋2，所用材料为 钢筋，直径较粗(直径大约在4-10mm左右)，排布数量较少，间距较宽。如图3所示，上下两 层同样的钢筋网片，通过少量连接筋4固定，连接方式较简易，主要起整体固定作用。可见， 目前使用的上下网片组合的钢筋骨架，其配筋量较少，钢筋分布间距很大，对板材的荷载有 一定的影响，且上下网片连接后仅起固定作用，没有...
【技术保护点】
一种钢丝网蒸压加气混凝土板，其特征在于，包括加气混凝土板体以及内衬于加气混凝土板体内的钢丝网骨架；该钢丝网骨架由数根钢丝形成的网状结构组成，所述钢丝的直径为１．５－３．０毫米。
【技术特征摘要】
【专利技术属性】
技术研发人员：许彬彬，李立安，郑炳芳，陈海鸣，刘于昌，袁翔，刘文龙，
申请(专利权)人：上海富春建业科技股份有限公司，
类型：发明
国别省市：31