本发明专利技术提供一种干挂胶用快速固化剂，所述固化剂为硫脲或聚醚改性胺类化合物。该快速固化剂结合了硫脲快速、低温反应性能和聚醚的高韧性，将毒性较大的胺类化合物嫁接在聚醚大分子上，系统分子链增长，使整个体系毒性降低至胺类化合物１／１０００以下；提高了固化剂活性和稳定性，低温反应活性增强，固化速度提高，Ａ、Ｂ组分配比宽容度增加到１∶０．６～１．５，不会造成任何缺陷。本发明专利技术还提供该快速固化剂的制备工艺及含有该快速固化剂的干挂胶。

Quick curing agent for dry adhesive and dry adhesive and its preparation process

The present invention provides a quick curing agent for dry adhesive. The curing agent is an amide compound modified with thiourea or polyether. The fast curing agent with high toughness, low temperature performance and fast reaction of thiourea polyether, the toxicity of amines in grafted polyether polymer, molecular chain growth, make the whole system to decrease the toxicity of amines 1 / 1000; improve the curing agent activity and stability, enhanced low temperature curing reaction activity. To improve the speed of A, and B ratio tolerance increased to 1: 0.6 to 1.5, will not cause any defects. The invention also provides the preparation process of the quick curing agent and the dry hanging glue containing the fast curing agent.

【技术实现步骤摘要】

本专利技术涉及一种干挂胶用快速固化剂，同时涉及生产该快速固化剂的工艺及含有 该固化剂的干挂胶。
技术介绍
干挂胶是石材粘接领域的结构性胶黏剂，现有的干挂胶大部分为双组分A组分 由双酚A类环氧树脂、填料和触变剂组成；B组分由胺类固化剂、填料和触变剂组成。在环 氧树脂固化剂中，胺类固化剂种类多、用量大，常温下挥发性大、毒性大，不利于施工人员健 康；A、B组分配比要求严格，不利于现场施工，施工中搅拌不充分，A组分过量会出现固化不 完全，粘接强度严重下降，B组分过量会出现过量的胺类迁移严重污染石材；低温下固化缓 慢，冬季室外施工难以进行，延缓工期。
技术实现思路
本专利技术所要解决的技术问题在于克服上述现有技术之不足，提供一种干挂胶用快 速固化剂。本专利技术所要解决的另一技术问题在于克服上述现有技术之不足，提供一种干挂胶 用快速固化剂的制备工艺。按照本专利技术提供的一种干挂胶用快速固化剂，所述固化剂为硫脲、聚醚改性胺类 化合物。所述快速固化剂为具有结构式(I)的化合物权利要求1.一种干挂胶用快速固化剂，其特征在于所述固化剂为硫脲或聚醚改性胺类化合物。2.如权利要求1所述的干挂胶用快速固化剂，其本文档来自技高网...

【技术保护点】
１．一种干挂胶用快速固化剂，其特征在于所述固化剂为硫脲或聚醚改性胺类化合物。