一种新型的铜合金及铜合金管制造技术

本发明专利技术提供了一种抗拉强度优异的铜合金和由所述铜合金制备而成的铜合金管，其主要成分有如下组成：Sn：0.15～0.95质量％，P：0.01～0.060质量％，B：0.001～0.01质量％，余量有铜和其它杂质组成，杂质含量小于0.06质量％。经过退火处理的铜合金管，其纵向抗拉强度σb≥250N/mm2，径向平均晶粒≤0.035mm，设纵向拉伸试验的屈服(极限)强度σ0.2，屈强比σ0.2/σb≤0.27。相对于磷脱氧铜制做的铜合金管，抗拉强度提高，晶粒细化，屈服强度无明显变化，耐蚀性及耐热性良好。

A new type of copper alloy and copper alloy tube

The invention provides a copper alloy tube of copper alloy an excellent tensile strength and the copper alloy was prepared, its main ingredients are as follows: Sn:0.15 to 0.95 mass%, P:0.01 to 0.060 mass%, B:0.001 to 0.01 mass%, residual copper and other impurities, impurity content less than 0.06 mass%. After copper alloy tube annealing, the longitudinal tensile strength B is larger than 250N/mm2, the radial average grain yield is less than or equal to 0.035mm, with longitudinal tensile test (Ultimate) strength is 0.2, the yield ratio is less than 0.27 sigma Sigma 0.2/ B. Compared with the copper alloy tubes made of phosphorus deoxidized copper, the tensile strength increases, grain refinement and yield strength have no obvious change, and the corrosion resistance and heat resistance are good.

【技术实现步骤摘要】

本专利技术涉及一种铜基合金，特别涉及一种高强度的铜合金及由所述铜合金制备的 铜合金管。
技术介绍
通常，制冷空调用热交换器(蒸发器、冷凝器)、连接管(室内外连机用)以及各种 铜合金管多采用磷脱氧铜(TP2)，是由于磷脱氧铜具有良好的热传导性能，且塑性好、易加 工和易焊接。目前，在空调用制冷剂市场，发展中国家大都采用HCFC (氢氯氟烃)系氟利昂，以 该系列的R22为例，管道工作压力最大为1. 5MPa, R22对地球大气臭氧层的破坏系数较大。 而欧美、日本等一些发达国家已开始全面使用对地球臭氧层破坏系数较小的HFC系氟利 昂，如R410A，管道工作压力最大2. 25MPa。此外在一些热泵热水器、大型超市的冷柜机以及 一些汽车空调领域已开始应用纯天然的更加环保的(X)2做制冷剂，管道工作压力最大达到 9 12MPa。也就是说，未来做为制冷空调用的铜合金管包括热交换器用管、连接管以及各 种铜合金管必须具有耐高压的能力，现有的磷脱氧铜合金管通过增加壁厚或许可以满足要 求，但外径不变的情况下，壁厚增加将会使铜合金管的流通面积减小，制冷剂的单位流量也 就减少，从而影响热交换能力。如果使铜合金本文档来自技高网...

【技术保护点】
一种铜合金，其特征在于，所述铜合金含有Ｓｎ：０．１５～０．９５质量％，Ｐ：０．０１～０．０６０质量％，Ｂ：０．００１～０．０１质量％，余量为铜及不可避免的杂质。