聚醚型聚氨酯丙烯酸酯及其制备方法技术

本发明专利技术提供了一种聚醚型聚氨酯丙烯酸酯及其制备方法，包括如下重量份的组分：聚醚多元醇４０～６０份，多己氰酸酯１０～３０份，丙烯酸羟丙酯或丙烯酸羟乙酯１０～３０份，三乙胺或二丁基二月桂酸锡０．１～０．５份，无水乙醇５～１０份，对羟基苯甲醚或２．６－二叔丁基对甲酚０．１～０．８份，三丙二醇二丙烯酸酯５～２０份，ＴＭＰＴＡ５－２０份，硝基苯０．０１－０．０２份。本发明专利技术具有优异的机械耐磨性和柔韧性，短裂伸长率高，涂膜具有优良的耐化学品性和耐高温，低温性能，附着力好．与环氧丙烯酸酯拼合使用效果更佳，也是成本最低的一类聚氨酯丙烯酸酯。

Polyether type polyurethane acrylate and preparation method thereof

The invention provides a polyether polyurethane acrylate and its preparation method, which comprises the following components by weight: polyether polyols 40 ~ 60, 10 ~ 30 multi cyanate ester, hydroxypropyl acrylate or 2-hydroxyethyl acrylate from 10 to 30, three or two butyl two triethylamine dilaurates 0.1 ~ 0.5 copies of ethanol 5 to 10 copies, 4-methoxyphenol or 2.6 BHT from 0.1 to 0.8, three propylene glycol acrylate two 5 ~ 20, TMPTA5 - 20, 0.01 - 0.02 of nitrobenzene. The present invention has excellent mechanical abrasion resistance and flexibility, short crack elongation, the coating has good chemical resistance and high temperature resistance, low temperature performance, good adhesion. Better effect with epoxy acrylate hybrid, but also the lowest cost for a class of polyurethane acrylate.

【技术实现步骤摘要】

本专利技术涉及一种聚氨酯丙烯酸酯及其制备方法。技术背景 ' _在紫外光(uv)固化的低聚物中，聚氨酯丙烯酸酯是仅次于环氧丙烯酸酯的第二类光固化物.这主要是由于聚氨酯丙烯酸酯的合成灵活性，柔 韧性，硬度，固化速度等可以事先设计进行控制。如石智强、季宁宁在<化工生产与技术>2007年14巻第5期发表的《紫外光固化聚氨酯丙烯酸酯树 脂合成与性能研究〉>和在<广州化学>2007年32巻第3期发表的《紫外光 固化聚氨酯丙烯酸树脂的研究发展》，采用上述文献报道的技术，存在加 料繁琐，温度不易控制，容易产生聚合现象。
技术实现思路
本专利技术的目的是提供一种，以克 服现有技术存在的上述缺陷。本专利技术的聚醚型聚氨酯丙烯酸酯包括如下重it份的组分聚醚多元醇40~60份多已氰酸酯10 30份丙烯酸羟丙酯或丙烯酸羟乙酯10 30份三乙胺或二丁基二月桂酸锡0.1~0,5份无水乙醇5~10份对羟基苯甲醚或2.6-二叔丁基对甲酚0.1 0.8份三丙二醇二丙烯酸酯 5 20份TMPTA 5 20份 硝基苯 0.01 0.02份。加入硝基苯是为了防止气象胶化；所说的聚醚多元醇的分本文档来自技高网...

【技术保护点】
聚醚型聚氨酯丙烯酸酯，其特征在于，包括如下重量份的组分：　聚醚多元醇　４０～６０份　多已氰酸酯　１０～３０份　丙烯酸羟丙酯或丙烯酸羟乙酯　１０～３０份　三乙胺或二丁基二月桂酸锡　０．１～０．５份　无水乙 醇　５～１０份　对羟基苯甲醚或２．６－二叔丁基对甲酚　０．１～０．８份　三丙二醇二丙烯酸酯　５～２０份　ＴＭＰＴＡ　５～２０份　硝基苯　０．０１～０．０２份。

【技术特征摘要】

【专利技术属性】
技术研发人员：叶荣森，关存洲，
申请(专利权)人：上海富臣化工有限公司，深圳市展辰达化工有限公司，北京展辰化工有限公司，
类型：发明
国别省市：31[中国|上海]