一种组成和结构可设计的氧化钇基透明陶瓷的制备方法技术

本发明专利技术属于陶瓷制备领域，具体涉及一种组成和结构可设计的氧化钇基透明陶瓷的制备方法。本发明专利技术利用流延成型的方法将激光离子掺杂的氧化钇基陶瓷粉体制备成流延膜，将具有不同组分的流延膜，通过组成和结构设计，叠层制备出既有复杂形状又具有特定组成和性能的陶瓷素坯，素坯脱粘后，再次经过冷等静压，素坯密度和均匀性明显好于干压成型的样品。本发明专利技术的烧结方法与现有技术相比能够得到更高性能的透明陶瓷。

Method for preparing yttrium oxide based transparent ceramic with composition and structure

The invention belongs to the field of ceramic preparation, in particular to a preparation method of an yttrium oxide base transparent ceramic with a composition and structure. The invention uses the method of casting the yttrium oxide based ceramic powder laser doped by casting film, cast film with different composition, the composition and structure design of laminated preparation which has complex shape and has a specific composition and properties of ceramic blank, blank after debonding. Again after cold isostatic pressing, green density and uniformity is better than dry pressed samples. Compared with the prior art, the sintering method of the invention can obtain transparent ceramics with higher performance.

【技术实现步骤摘要】

本专利技术属于陶瓷成型和设计制备领域，具体涉及一种组成和结构可设计的氧化钇基透明陶瓷的制备方法。
技术介绍
透明陶瓷既具有像玻璃一样的透光性，又具有陶瓷本身的耐高温、耐腐蚀、高强t: 等优异性能。在能源、医学成像、激光武器、勘探等方面透明陶瓷均有广泛应用前景。高性 能透明陶瓷是当前材料领域研究和应用的重要前沿方向。氧化钇基透明陶瓷是透明陶瓷领 域的典型代表之一。 目前透明陶瓷主要采用干压结合冷等静压方法成型。如陈积阳等申请的中 国专利03129618. 3等，也有部分注桨成型的报道如。干压和冷等静压结合的方法具有工艺简单、操作方便等优点。但是对于纳米级 粉体，由于粉体极细，干压时颗粒间摩擦力较大，不易压实，导致烧结不致密。此外，干压结 合冷等静压的方法只能制备一些块状、圆片状等形状简单的样品，不能制备复杂形状透明 陶瓷。 特别地，通常用做透明光学材料的单晶的掺杂都是均匀掺杂，无法实现具有一定设计的梯度掺杂。研究表明，梯度掺杂的激光器材料在工作时可以更好地散热，有利于提高 其工作功率。氧化钇基具有较高的热导率，但是掺入少量离子后其热导率显著下降。梯度设计的氧化钇基透明陶瓷可以使陶瓷本文档来自技高网...

【技术保护点】
一种组成和结构可设计的氧化钇基透明陶瓷的制备方法，包括如下步骤：　　１）将含有不同掺杂含量的氧化钇粉体分别流延成膜；　　２）将具有不同掺杂含量的流延膜根据需求加工成不同的形状，然后根据叠层设计进行叠层；　　３）将叠层后的流延膜进行冷等静压处理，然后经脱粘处理后再次进行冷等静压处理；　　４）将冷等静压处理后的样品进行真空烧结。

【技术特征摘要】

【专利技术属性】
技术研发人员：黄毅华，江东亮，张景贤，林庆玲，黄政仁，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明
国别省市：31[中国|上海]