The invention provides a two component high-strength spraying polyurethane waterproof coating. It consists of A and B components according to the volume ratio of 1: 1; wherein, the component A by low functionality isocyanate and polyether polyols synthesized by semi prepolymer; by weight, polyisocyanate is 50 ~ 80, 2 ~ 2.4 functionality polyether; alcohol is 20 ~ 50, 2 ~ 4 degrees, can; B component comprises 40 to 84 portions of polyether polyols or amine terminated polyether or mixtures of 10 ~ 40 amine chain extender chain extender or alcohol or a mixture of 0 to 20 portions of fillers and additives. The present invention has similar or even higher mechanical properties and waterproofing material and the construction method of spraying, convenient and efficient, and greatly prolongs the service life of the waterproof material, non solvent system also greatly ensure the material requirements of environmental protection, more reliable and more efficient, more environmentally friendly. Compared with the traditional waterproof material, it can have high strength and high elongation at the same time.
【技术实现步骤摘要】
本专利技术涉及一种聚氨酯防水涂料，具体来说涉及一种双组分高强喷涂聚氨酯防水涂料， 它可用于各种建(构)筑物的防水工程。
技术介绍
在建(构)筑物的防水领域，主要以巻材和涂料两大类材料为主。巻材施工存在的弊端 是对基层含水率要求高，基层形状复杂时铺贴困难，多块拼接会影响美观；另外巻材接缝多 且接缝不严密易造成串水，最终出现渗漏，漏水后的维修也是难题；再则国内配套胶黏剂性 能差，施工质量难以保证。防水涂料主要包括水性丙烯酸、硅橡胶和聚氨酯等，可以克服上述巻材存在的不足。其 中聚氨酯涂料是20世纪后期发展起来的一种新型材料，在上世纪70年代进入我国防水材料 市场，被广泛用于屋面、地下工程与厨卫间，取得了良好的防水效果。但是这些防水涂料都 存在如下明显的不足施工方式为涂刮，由于固化时间长，立面厚涂时容易流挂，需多道施 工才能达到设计厚度且涂层之间的施工间隔时间长，导致施工效率低；涂膜延伸率高而拉伸 强度及撕裂强度不足，在施工过程中容易受到外力损伤；并且粘结强度较低，与混凝土的粘 结强度,特别是潮湿基面的粘结强度达不到高档建筑及高速铁路等国家重点工程对防水材料 的使用要求...
【技术保护点】
一种双组分高强喷涂聚氨酯防水涂料，其特征在于，它由Ａ组分和Ｂ组分按１∶１的体积比组成；其中，Ａ组分是由低官能度的多异氰酸酯和聚醚多元醇合成的半预聚物；按重量份计，多异氰酸酯是５０～８０份，官能度为２．０～２．４；聚醚多元醇是２０～５０份，官能度为２～４；Ｂ组分包括４０～８４份聚醚多元醇或端氨基聚醚或它们的混合物，１０～４０份胺类扩链剂或醇类扩链剂或它们的混合物，０～２０份颜填料及助剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：赵希娟，刘彦东，潘美，郑旗，王强，王炜，
申请(专利权)人：中冶集团建筑研究总院，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。