The invention provides a high chlorinated polyethylene coating containing stainless steel scales and a preparation method thereof. The coating comprises the following components in quality and according to the number of copies of the 100 parts: high chlorinated polyethylene resin, modified resin 10 ~ 250, 10 ~ 1400 stainless steel flakes, pigments and fillers from 0 to 1400, 0.1 to 10.5 portions of defoaming agent, coupling agent 0 ~ 175, 0.3 ~ 10.5 anti settling agent from 100 to 2000, solvent. The beneficial effect of the invention is: it has excellent corrosion resistance, can be widely used in acid, alkali, salt, water, soil, air and other chemical corrosive environment; prolong the life of the protective coating system; the invention can be used as a primer, intermediate coat, top or bottom surface of a coating, single component packaging, convenient construction, quick drying, construction in 20 ~ 40 C ambient temperature.
【技术实现步骤摘要】
本专利技术涉及一种，该涂料可以作为底漆、 中间漆、面漆或底面合一型防腐漆。
技术介绍
腐蚀特别是金属构件和混凝土结构的腐蚀给国家造成了巨大的损失，约占当年GDP的 3-5%，因此，防腐蚀工作显得非常重要。而在众多的防腐蚀手段中，防腐涂料一直是最主要、 最有效、最方便、最常用的方法。防腐涂料之所以能对构筑物及设施、设备具有较好的保护 效果，是因为涂料在成膜之后能有效地将腐蚀介质与基材隔离，在一定的时间内腐蚀介质不 能到达基材。因此，衡量涂料的防护效果，其抗介质渗透的能力是一个关键的参数。目前经常采用将玻璃鳞片或铝合金鳞片(俗称铝粉浆)作为填料加入到涂料中的办法， 由于其是片状结构，具有较大的径厚比，理想条件下这两类填料在成膜物质中可以有效延长介质渗透路径，提高涂料的抗渗透能力，从而达到提高涂料防腐寿命的目的。但是这类涂料 有其先天性弊病玻璃鳞片硬而脆，膨胀系数与成膜物质以及钢铁和混凝土基材差别很大， 在冷热循环的使用过程中导致漆膜内应力增加，造成漆膜开裂等弊病；同时玻璃鳞片与各种 树脂的粘接性不好，需要添加偶联剂对其进行表面处理，如果处理不好，沿着鳞片与树脂界 ...
【技术保护点】
一种含不锈钢鳞片的高氯化聚乙烯涂料，其特征在于，包括下列组分及按质量份数的含量： 高氯化聚乙烯树脂１００份 改性树脂１０～２５０份 不锈钢鳞片１０～１４００份 颜料、填料０～１４００份 消泡剂０．１～１０．５份 偶联剂０～１７５份 防沉剂０．３～１０．５份 溶剂１００～２０００份。
【技术特征摘要】
【专利技术属性】
技术研发人员：邢峻，郑旗，王炜，程振强，徐志平，于钦萍，刘毅，段春华，崔梓杰，
申请(专利权)人：中冶集团建筑研究总院，
类型：发明
国别省市：11[中国|北京]